Styrolution LuranÂ® S 778 T ASA

Category	Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer	Styrolution
Trade Name	Luran®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styrolution LuranÂ® S 778 T ASA.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Luran S 778 T is an injection molding ASA grade with enhanced toughness and heat resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/inÂ³	ISO 1183
Water Absorption	1.65 %	1.65 %	ISO 62
Moisture Absorption at Equilibrium	0.35 %	0.35 %	23Â°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.0055 cm/cm	0.0055 in/in	ASTM Data; MD
Linear Mold Shrinkage, Flow	0.0045 cm/cm	0.0045 in/in	ISO Data
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	ISO Data
Melt Flow	1.1 g/10 min @Load 3.80 kg, Temperature 230 Â°C	1.1 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM Test
	5.0 g/10 min @Load 10.0 kg, Temperature 220 Â°C	5.0 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ISO 1133
	5.0 g/10 min @Load 10.0 kg, Temperature 220 Â°C	5.0 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM Test

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	110	110	ASTM Test
Tensile Strength, Yield	49.0 MPa	7110 psi	2 in/min; ASTM Test
	54.0 MPa	7830 psi	50mm/min; ISO 527
	24.0 MPa @Temperature 80.0 Â°C	3480 psi @Temperature 176 Â°F	ISO Data
	79.0 MPa @Temperature -40.0 Â°C	11500 psi @Temperature -40.0 Â°F	ISO Data
Elongation at Break	8.0 %	8.0 %	50mm/min, Nominal strain; ISO 527
	20 %	20 %	2 in/min; ASTM Test
Elongation at Yield	3.4 %	3.4 %	50mm/min; ISO 527
	2.2 % @Temperature 80.0 Â°C	2.2 % @Temperature 176 Â°F	ISO Data
	5.0 % @Temperature -40.0 Â°C	5.0 % @Temperature -40.0 Â°F	ISO Data
Tensile Modulus	2.36 GPa	342 ksi	ASTM Test
	2.50 GPa	363 ksi	1mm/min; ISO 527
Flexural Strength	71.0 MPa	10300 psi	ASTM Test
	80.0 MPa	11600 psi	ISO Data
Flexural Modulus	2.50 GPa	363 ksi	ASTM Test
Izod Impact, Notched	0.370 J/cm @Temperature -40.0 Â°C	0.693 ft-lb/in @Temperature -40.0 Â°F	ASTM Test
	2.50 J/cm @Thickness 3.17 mm	4.68 ft-lb/in @Thickness 0.125 in	ASTM Test
Charpy Impact Unnotched	25.0 J/cmÂ²	119 ft-lb/inÂ²	ISO 179
	9.00 J/cmÂ² @Temperature -30.0 Â°C	42.8 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179
Charpy Impact, Notched	1.50 J/cmÂ²	7.14 ft-lb/inÂ²	ISO 179
	0.400 J/cmÂ² @Temperature -30.0 Â°C	1.90 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179
Dart Drop, Total Energy	47.0 J	34.7 ft-lb	ASTM Test
Impact Test	44.0 J	32.5 ft-lb	Instrumented Dart Impact (Energy at Peak Force); ASTM Test
Tensile Creep Modulus, 1000 hours	1250 MPa	181000 psi	ISO 899

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	95.0 Âµm/m-Â°C	52.8 Âµin/in-Â°F	ISO 11359
Deflection Temperature at 0.46 MPa (66 psi)	106 Â°C	223 Â°F	annealed; ASTM Test
	106 Â°C	223 Â°F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	103 Â°C	217 Â°F	annealed; ASTM Test
	103 Â°C	217 Â°F	ISO 75
Vicat Softening Point	104 Â°C	219 Â°F	Rate "A" Loading 2 (50 degC/h 50N); ASTM Test
	104 Â°C	219 Â°F	(50 Â°C/h / 50N) - B/50; ISO 306
Flammability, UL94	HB @Thickness 1.58 mm	HB @Thickness 0.0622 in
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
Oxygen Index	19 %	19 %	ISO 4589-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+12 ohm-cm	>= 1.00e+12 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+13 ohm	>= 1.00e+13 ohm	IEC 60093
Dielectric Constant	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	IEC 60250
	3.9 @Frequency 100 Hz	3.9 @Frequency 100 Hz	IEC 60250
Dielectric Strength	35.0 kV/mm	889 kV/in	IEC 60243-1
Dissipation Factor	0.0090 @Frequency 100 Hz	0.0090 @Frequency 100 Hz	IEC 60250
	0.033 @Frequency 1.00e+6 Hz	0.033 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	250 Â°C	482 Â°F	Injection molding
	241 - 279 Â°C	466 - 534 Â°F	Injection Molding
Mold Temperature	60.0 Â°C	140 Â°F	Injection molding
	40.6 - 79.4 Â°C	105 - 175 Â°F	Injection Molding
Injection Velocity	200 mm/sec	7.87 in/sec	Injection molding
Drying Temperature	79.0 Â°C	174 Â°F	Injection Molding
Dry Time	2 - 4 hour	2 - 4 hour	Injection Molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	North America and Europe
Form	Pellets
Impact Modified	Yes
Injection Molding Regrind	<30%
NSF Std. 51	No
NSF Std. 61	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat
	Light stabilized or stable to light
	Release agent
	U.V. stabilized or stable to weather
UL.UL-C	Yes
USP Class VI	No