Nylene® PA6/6 Glass Filled 5133 HS Nylon 6/6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Nylene® |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nylene® PA6/6 Glass Filled 5133 HS Nylon 6/6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
33% Glass Filler; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 254 °C | 489 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 HI-M PA6 with improved impact strength
- Gwent Electronic Materials C2050517D1 Carbon Graphite Ink
- Tisan TISARBON® 10% Glass Fiber Reinforced Polycarbonate
- EDRO EDRO400™ #40 Prehardened Insert Quality Martensitic Stainless Steel
- ChevronTexaco Delo® 400 SAE 50
- Eagle Brass 1008 Low Carbon Steel, Full Hardened
- Arlon 55103R030 0.030" (0.762 mm) Cured Silicone Rubber with Fiberglass Substrate
- Petroquimica Triunfo Trithene® TX 4003 LDPE and LLDPE Blend - High Resistance Film
- SK Chemicals SKYTHANE® 398A S series Polyurethane
Copyright © lookpolymers.com All Rights Reserved