Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Molding M3500 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Molding M5240 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Molding M5700 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Molding M5731 Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. Dark colored compounds do not.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
PolyOne Stat-Tech™ NJ-10SS/000 Nylon 12 - 10% Stainless Steel Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Stat-kon CX01039 PS (Europe-Africa-Middle East) LNP* Stat-kon* CX01039 is a compound based on Polystyrene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
Techmer ES HiFill FR® ABS FR Availability: North AmericaForms: PelletsFeatures: Flame RetardantTPCI# 1039121Information provided by TP Composites, Inc. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON KX96321 POM LNP* STAT-KON* KX96321 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Asia Pacific) PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xylex X7300OQ PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. High flow with good impact and excellent optical quality.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP 9X04488 PPS LNP* THERMOCOMP* 9X04488 is a compound based on PPS resin containing Mineral. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
Techmer ES Plastiblend® ABS 8009 FR Availability: North AmericaForms: PelletsFeatures: Flame Retardant and High Heat ResistanceInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp 9X04488 POLYPHENYLENESULFONE LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D 790 |
SABIC Innovative Plastics Noryl EBN90 PPE+HIPS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | |
Cosmic Plastics 306 Orlon Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® E-17222 High Impact Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
Unitika TERRAMAC TP-4030 Polylactic Acid (PLA) Soft, Extrusion, blow, and foam sheet grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6 Information provided by A. Schulman. |
|||
Flexural Strength | 71.0 MPa @Strain 5.00 % |
10300 psi @Strain 5.00 % |
ASTM D790 |
Eastman Spectar® Clear Copolyester for Thermoforming Applications:Decorative Light-Transmitting PanelsHeavy gauge sheet displaysKey Attributes:Easy to print and decorateExcellent clarityExcellent thermoforming characteristicsGood chemical resistanceOd.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | JIS-K-6740 |
Denka VINYKON R2001 PVC, R grade for hard extrusion A PVC resin compound offering excellent physical properties and workability. A broad product lineup is available, including hard and soft grades, as well as those for extrusion and injection molding.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
Ensinger Tecatron® XP-71 Compression Molded PPS Compound, 20% PTFE Filled Natural Ensinger Special Polymers has over twenty different grades of TECATRON PPS available. Custom formulations can be blended to suit specific applications. Compression molding is amenable to short run p.. |
|||
Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-777E ABS - High Heat Ultra High Heat |
|||
Flexural Strength | 71.0 MPa | 10300 psi | |
Abatron AboCast 8503-3/AboCure 8503-3 Colorless Epoxy AboCast 8503-3/AboCure 8503-3 is a general purpose, medium speed, colorless epoxy casting compound with low viscosity. It has a good balance of properties with a fairly fast hardening. Suggested Use.. |
|||
Flexural Strength | <= 71.0 MPa | <= 10300 psi | ASTM D790 |
Arkema Group Solarkote® A200 Acrylic Superior UV protection and weatherability, ASTM Classification PMMA 0233V1Information provided by Arkema Group |