Styrolution LuranÂ® S 778 Q42 Colored ASA

Category	Polymer , Thermoplastic , ASA Polymer
Manufacturer	Styrolution
Trade Name	Luran®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styrolution LuranÂ® S 778 Q42 Colored ASA.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Injection molding grade with enhanced toughness and resistance to heat distortion. Especially suitable for exterior automotive components (e.g. radiator grills, rear end appliquÃ© panels and mirror housings).Information provided by STYROLUTION, which is a joint venture between BASF and INEOS

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/inÂ³	ISO 1183
Water Absorption	1.65 %	1.65 %	Equilibrium; ISO 62
	0.45 % @Time 86400 sec	0.45 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	0.35 %	0.35 %	23Â°C/50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in
Melt Flow	5.35 g/10 min @Load 10.0 kg, Temperature 220 Â°C	5.35 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	85.0 MPa @Load 36.5 kg, Time 30.0 sec	12300 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Tensile Strength, Yield	54.0 MPa	7830 psi	50 mm/min; ISO 527-1/-2
Elongation at Break	8.0 %	8.0 %	Nominal, 50 mm/min; ISO 527-1/-2
Elongation at Yield	3.4 %	3.4 %	50 mm/min; ISO 527-1/-2
Tensile Modulus	2.50 GPa	363 ksi	ISO 527-1/-2
Flexural Strength	80.0 MPa	11600 psi	ISO 178
Izod Impact, Notched	2.50 J/cm	4.68 ft-lb/in	ASTM D256
Charpy Impact Unnotched	9.00 J/cmÂ² @Temperature -30.0 Â°C	42.8 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eU
	25.0 J/cmÂ² @Temperature 23.0 Â°C	119 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eU
Charpy Impact, Notched	0.400 J/cmÂ² @Temperature -30.0 Â°C	1.90 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	1.50 J/cmÂ² @Temperature 23.0 Â°C	7.14 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	1250 MPa @Strain <=0.500 %	181000 psi @Strain <=0.500 %	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 - 110 Âµm/m-Â°C @Temperature 23.0 - 80.0 Â°C	44.4 - 61.1 Âµin/in-Â°F @Temperature 73.4 - 176 Â°F	ISO 11359-1/-2
Thermal Conductivity	0.170 W/m-K	1.18 BTU-in/hr-ftÂ²-Â°F	DIN 52612-1
Maximum Service Temperature, Air	90.0 Â°C	194 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	106 Â°C	223 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	103 Â°C	217 Â°F	ISO 75-1/-2
Vicat Softening Point	104 Â°C	219 Â°F	VST/B/50; ISO 306
	113 Â°C	235 Â°F	VST/A/50; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10
	HB @Diameter 4.00 mm	HB @Diameter 0.157 in	IEC 60707

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	IEC 60093
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 60093
Dielectric Constant	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	IEC 60250
	3.9 @Frequency 100 Hz	3.9 @Frequency 100 Hz	IEC 60250
Dielectric Strength	35.0 kV/mm	889 kV/in	K20/P20; IEC 60243-1
Dissipation Factor	0.0090 @Frequency 100 Hz	0.0090 @Frequency 100 Hz	IEC 60250
	0.033 @Frequency 1.00e+6 Hz	0.033 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test Liquid A; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	240 - 280 Â°C	464 - 536 Â°F	Injection
Mold Temperature	40.0 - 80.0 Â°C	104 - 176 Â°F	Injection
Drying Temperature	80.0 Â°C	176 Â°F	Pre-drying
Dry Time	2 - 4 hour	2 - 4 hour	Pre-drying

Descriptive Properties	Value	Comments
Color	Black 23609 Q42
	Black 25991 Q42
	Black 33753 Q42
	Black 36733 Q42
	Black 36831 Q42
	Black 89737 Q42
	Brown 37032 Q42
	Gray 35316 Q42
	Gray 37192 Q42
	Gray 427345 Q42
Commercial Status	Europe
Primary Processing Technique	Injection Molding