SABIC Innovative Plastics LNP STAT-LOY KX05015 Acetal Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY KX05015 Acetal Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Loy* KX05015 is a compound based on Acetal Copolymer resin containing Antistat. Added features include permanent Anti-Static.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 7.9 % @Time 86400 sec |
7.9 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.028 cm/cm | 0.028 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 18.7 % | 18.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.40 GPa | 203 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 48.0 MPa | 6960 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.40 GPa | 203 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 157 µm/m-°C @Temperature 23.0 - 60.0 °C |
87.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 160 µm/m-°C @Temperature 23.0 - 60.0 °C |
88.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+10 - 1.00e+12 ohm | 1.00e+10 - 1.00e+12 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Permabond Anti-Seize Compound Lubricant
- SABIC Innovative Plastics LNP LUBRICOMP DL0029E PC
- Ineos ABS NOVODUR® P2L-AT ABS, Injection Grade (discontinued **)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 2.0 PHR Sulfur
- American Elements Nickel Oxide Nanopowder
- DuPont Elvax® 550 Ethylene-Vinyl Acetate Copolymer Resin
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction
- BASF Hydroxypivalic Acid Neopentylglycolester Molten (HPN)
- ATI Allegheny Ludlum Stainless Steel Type 201L, 20% Cold Work (UNS S20103)
Copyright © lookpolymers.com All Rights Reserved