Solvay Technyl® A218V43 43% Glass Filled, Heat Stabilized Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A218V43 43% Glass Filled, Heat Stabilized Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183-A |
| Water Absorption | 0.70 % | 0.70 % | 24 Hr.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 13.8 GPa | 2000 ksi | ISO 527 |
| Flexural Strength | 310 MPa | 45000 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263.0 °C | 505.4 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Compression Zone |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Nozzle Temperature | 271 - 279 °C | 520 - 535 °F | |
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- Nylene® 401D, Nylon 6
- Nilit FRIANYL A63 V0 G5 Nylon 6.6 for injection molding, 25% glass fiber reinforced
- Chevron Phillips 4522 LDPE Shrink and Heavy Duty Packaging Film Resin (discontinued **)
- Multibase Multi-Flex® RP 6568 C Natural TPE Thermoplastic Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT (Europe-Africa-Middle East)
- Hexcel® HexWeb® HRH-10 - 1/8- 4.0 Aramid Fiber/Phenolic Resin Honeycomb
- TSE Industries Millathane® CM High Temperature-Resistant Millable Polyester Polyurethane
- ChevronTexaco ECO® ISO 46 Hydraulic Oil AW
- Ascend Performance Materials Vydyne® R533H BK02 Nylon 66, 33% Glass Reinforced, DAM
- SABIC Innovative Plastics Valox® V9561 PET (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved