Solvay Technyl® A218 Heat Stabilized Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A218 Heat Stabilized Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 24 Hr.; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 90.3 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ASTM D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ASTM D790 |
| Izod Impact, Notched | 0.502 J/cm | 0.940 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 438 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 270 °C | 482 - 518 °F | |
| Middle Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Compression Zone |
| Front Barrel Temperature | 270 - 300 °C | 518 - 572 °F | |
| Nozzle Temperature | 280 - 290 °C | 536 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Fill Speed | 300 - 600 mm/sec | 11.8 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 50 - 150 cm3/sec |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6 HI PA6 with improved impact strength
- Momentive Performance Materials RTV627 Dark Gray General Purpose Potting/Encapsulating Compound
- SABIC Innovative Plastics NORYL GFN2V PPE+HIPS (Europe-Africa-Middle East)
- ExxonMobil LDPE LD 319.92 Low Density Polyethylene Resin
- Arlon Red Silicone Press Pad with sandwiched Fiberglass Substrate (55393R062)
- BASF Ultramid® B29 HM 01 PA6 (Dry)
- Polyplastic Armlen® PP 12IM-895 Impact Modified Polypropylene
- Dow PELLETHANE® 2103-75D Film Grade Thermoplastic Polyurethane Elastomer (discontinued **)
- SMAC SMACMOUNT® 1242S Damping Material
Copyright © lookpolymers.com All Rights Reserved