Solvay TECHNYL® C 52G1 V25 Grey R7035 (XC 1329/A) PA6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 52G1 V25 Grey R7035 (XC 1329/A) PA6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 6, Glass-filled, glow-wire modified, color stabilized, lubricated for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: TECHNYL C 52G1 V25 GREY R7035 CF is used in all sectors of industry, offering good glow wire performance and heat resistance, color stability and productivity. This grade is specifically suited for MCB's and low voltage switches. This product is available in Electrical Grey color as standard.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183/A |
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0085 cm/cm | 0.0085 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 Type 1A |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 Type 1A |
| Tensile Modulus | 6.85 GPa | 994 ksi | ISO 527 Type 1A |
| Izod Impact, Notched (ISO) | 4.70 kJ/m² | 2.24 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 4.10 J/cm² | 19.5 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
1210 |
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
1210 | |
| Glow Wire Test | 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
ISO 60695-2-12 |
| 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 235-245°C |
Users viewing this material also viewed the following:
- Noble Polymers Ecobarrier™ 0712 Thermoplastic Olefin (TPO)
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer (discontinued **)
- Mallard Creek Polymers ROVENE® 6487 Styrene-Acrylic Emulsion
- LG Chemical SBR 1789 High Acrylonitrile Polymer
- SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP
- UBE 5021T Nylon 6/66 Monofilament (Drawing Ratio=5)
- Westlake Tymax™ GT4157 Anhydride Modified Linear Low Density Polyethylene
- Epoxy Technology EPO-TEK® E2116 Electrically Conductive, Silver Epoxy
- BASF Nypel® RC6024 BK 30% Mineral/Glass Filled PA6 (Dry)
- Epoxyset Epoxibond EB-177 Unfilled Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved