- Asia International Enterprise (Hong Kong) 30G6 Polybutylene terephthalate, 30% Glass Fiber Filled
Asia International Enterprise (Hong Kong) 30G6 Polybutylene terephthalate, 30% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 30G6 Polybutylene terephthalate, 30% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc @Temperature 23.0 °C |
1.52 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage | 0.0040 - 0.011 cm/cm | 0.0040 - 0.011 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 123 MPa | 17800 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 177 MPa | 25700 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 7.65 GPa | 1110 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.47 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 230 - 265 °C | 446 - 509 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour |
Users viewing this material also viewed the following:
- Abatron UWBONDL A/B Filled Potting Compound (discontinued **)
- Victrex® Vicote® F816 Black Polyetheretherketone (PEEK) Liquid Dispersion
- Schott Glass 8326 Neutral Glass Tubing
- Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA), 33% Glass Fiber
- SABIC Innovative Plastics Noryl PC180X PPE+PS
- Unifrax FyreWrap® MAX 2.0 Duct Insulation Two-Layer ASTM E-2336 System
- A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene
- Hexcel® HexPly® 954-3 Curing Cyanate Resin, M55J Fiber
- Eurostar Staramide A28N PA66, Nucleated, Injection Molding
Copyright © lookpolymers.com All Rights Reserved