- Solvay TECHNYL® B 218L V30 Black 44 N PA66, 30% glass fiber, DRY
Solvay TECHNYL® B 218L V30 Black 44 N PA66, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® B 218L V30 Black 44 N PA66, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Copolyamide 66/6, reinforced with 30% of glass fiber, for injection molding, heat stabilized with improved UV ageing resistance.Available in: Asia Pacific, Europe and Latin AmericaProduct Applications: TECHNYL B 218L V30 noir 44N is used in all sectors of industry, offering an excellent combination of thermal and mechanical properties. This grade is commonly used for automotive applications which require a good surface appearance and a good UV resistance, such as: external mirror housings and door handles. This product is available in black color.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Water Absorption | 0.95 % @Temperature 23.0 °C, Time 86400 sec |
0.95 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0071 cm/cm | 0.0071 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | ISO 527 Type 1A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Tensile Modulus | 9.80 GPa | 1420 ksi | ISO 527 Type 1A |
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 |
| Flexural Modulus | 8.30 GPa | 1200 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
14.4 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 242 °C | 468 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 3.00e+13 ohm | 3.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 270 °C | 482 - 518 °F | |
| Front Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 260-270°C |
Users viewing this material also viewed the following:
- Overview of materials for Nylon 66, 10% Glass Fiber Filled
- Kuraray Genestarâ„¢ GA2330 Nylon, 33% Glass Filled
- LATI Latistat 52/7-02 PP Homopolymer
- Solvay TECHNYL® A 218 V15 PA66, 15% glass fiber, Conditioned
- Shin-Etsu Silicones KE-3611U Electrically Conductive Silicone Elastomer
- CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Conditioned
- Epoxy Technology EPO-TEK® E3035 Electrically Conductive Adhesive
- Dow R792-35RNA Polypropylene Random Copolymer Resin
- CMW® THERMKON® 70M Molybdenum Copper parts
- Akzo Nobel Expancel® 091 DU 80 Dry unexpanded microspheres
Copyright © lookpolymers.com All Rights Reserved