SABIC MG200024 Linear Low Density Polyethylene for Compounding

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Compounding Resin
Manufacturer SABIC
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC MG200024 Linear Low Density Polyethylene for Compounding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: MG200024 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution primarily suitable for compounding. It is in the powder form designed to give good flow properties with low temperature toughness, stress crack resistance and high gloss.Typical Applications: MG200024 is recommended for carpet backing, metal coating and compounding for masterbatch production.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
load density; ASTM D1505
ESCR 100% Igepal® 6.0 hour
6.0 hour
F50; ASTM D1693B
ESCR 10% Igepal® 3.0 hour
3.0 hour
F50; ASTM D1693B
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
ASTM D2240
Tensile Strength at Break 12.0 MPa
1740 psi
ASTM D638
Tensile Strength, Yield 10.0 MPa
1450 psi
ASTM D638
Elongation at Break >= 500 %
>= 500 %
ASTM D638
Flexural Strength 9.00 MPa
1310 psi
ASTM D790
Flexural Modulus 0.200 GPa
29.0 ksi
ASTM D790
1% Secant Modulus 230 MPa
33400 psi
ASTM D638
Izod Impact, Notched 5.00 J/cm
9.37 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 92.0 °C
198 °F
ASTM D1525
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746
Processing Properties Metric English Comments
Mold Temperature 15.0 - 60.0 °C
59.0 - 140 °F
Injection Pressure 60.0 - 100 MPa
8700 - 14500 psi