Outokumpu 153MA™ High Temperature Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 153MA™ High Temperature Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and creep resistance. For use over 550°C for equipment and components within: Iron, steel, and non-ferrous industriesEngineering industryEnergy conservation plantsCement industryAvailable in hot rolled plate (Quarto), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 7.80 g/cc
0.282 lb/in³
RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 660 MPa
95700 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
300 MPa

@Temperature 700 °C
43500 psi

@Temperature 1290 °F
EN min.
385 MPa

@Temperature 600 °C
55800 psi

@Temperature 1110 °F
EN min.; EN 10002-5
435 MPa

@Temperature 500 °C
63100 psi

@Temperature 932 °F
EN min.; EN 10002-5
470 MPa

@Temperature 400 °C
68200 psi

@Temperature 752 °F
EN min.; EN 10002-5
475 MPa

@Temperature 300 °C
68900 psi

@Temperature 572 °F
EN min.; EN 10002-5
485 MPa

@Temperature 200 °C
70300 psi

@Temperature 392 °F
EN min.; EN 10002-5
525 MPa

@Temperature 100 °C
76100 psi

@Temperature 212 °F
EN min.; EN 10002-5
570 MPa

@Temperature 50.0 °C
82700 psi

@Temperature 122 °F
EN min.; EN 10002-5
Tensile Strength, Yield 340 MPa

@Strain 0.200 %
49300 psi

@Strain 0.200 %
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
380 MPa

@Strain 1.00 %
55100 psi

@Strain 1.00 %
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
110 MPa

@Strain 0.200 %,
Temperature 700 °C
16000 psi

@Strain 0.200 %,
Temperature 1290 °F
EN min.
120 MPa

@Strain 0.200 %,
Temperature 600 °C
17400 psi

@Strain 0.200 %,
Temperature 1110 °F
EN min.; EN 10002-5
130 MPa

@Strain 0.200 %,
Temperature 500 °C
18900 psi

@Strain 0.200 %,
Temperature 932 °F
EN min.; EN 10002-5
135 MPa

@Strain 1.00 %,
Temperature 700 °C
19600 psi

@Strain 1.00 %,
Temperature 1290 °F
EN min.
140 MPa

@Strain 0.200 %,
Temperature 400 °C
20300 psi

@Strain 0.200 %,
Temperature 752 °F
EN min.; EN 10002-5
150 MPa

@Strain 1.00 %,
Temperature 600 °C
21800 psi

@Strain 1.00 %,
Temperature 1110 °F
EN min.; EN 10002-5
150 MPa

@Strain 0.200 %,
Temperature 300 °C
21800 psi

@Strain 0.200 %,
Temperature 572 °F
EN min.; EN 10002-5
160 MPa

@Strain 1.00 %,
Temperature 500 °C
23200 psi

@Strain 1.00 %,
Temperature 932 °F
EN min.; EN 10002-5
165 MPa

@Strain 0.200 %,
Temperature 200 °C
23900 psi

@Strain 0.200 %,
Temperature 392 °F
EN min.; EN 10002-5
170 MPa

@Strain 1.00 %,
Temperature 400 °C
24700 psi

@Strain 1.00 %,
Temperature 752 °F
EN min.; EN 10002-5
180 MPa

@Strain 1.00 %,
Temperature 300 °C
26100 psi

@Strain 1.00 %,
Temperature 572 °F
EN min.; EN 10002-5
195 MPa

@Strain 1.00 %,
Temperature 200 °C
28300 psi

@Strain 1.00 %,
Temperature 392 °F
EN min.; EN 10002-5
200 MPa

@Strain 0.200 %,
Temperature 100 °C
29000 psi

@Strain 0.200 %,
Temperature 212 °F
EN min.; EN 10002-5
235 MPa

@Strain 1.00 %,
Temperature 100 °C
34100 psi

@Strain 1.00 %,
Temperature 212 °F
EN min.; EN 10002-5
245 MPa

@Strain 0.200 %,
Temperature 50.0 °C
35500 psi

@Strain 0.200 %,
Temperature 122 °F
EN min.; EN 10002-5
280 MPa

@Strain 1.00 %,
Temperature 50.0 °C
40600 psi

@Strain 1.00 %,
Temperature 122 °F
EN min.; EN 10002-5
Elongation at Break 55 %
55 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Rupture Strength 4.00 MPa

@Temperature 1000 °C,
Time 3.60e+7 sec
580 psi

@Temperature 1830 °F,
Time 10000 hour
10.0 MPa

@Temperature 900 °C,
Time 3.60e+7 sec
1450 psi

@Temperature 1650 °F,
Time 10000 hour
16.0 MPa

@Temperature 850 °C,
Time 3.60e+7 sec
2320 psi

@Temperature 1560 °F,
Time 10000 hour
25.0 MPa

@Temperature 800 °C,
Time 3.60e+7 sec
3630 psi

@Temperature 1470 °F,
Time 10000 hour
41.0 MPa

@Temperature 750 °C,
Time 3.60e+7 sec
5950 psi

@Temperature 1380 °F,
Time 10000 hour
63.0 MPa

@Temperature 700 °C,
Time 3.60e+7 sec
9140 psi

@Temperature 1290 °F,
Time 10000 hour
98.0 MPa

@Temperature 650 °C,
Time 3.60e+7 sec
14200 psi

@Temperature 1200 °F,
Time 10000 hour
157 MPa

@Temperature 600 °C,
Time 3.60e+7 sec
22800 psi

@Temperature 1110 °F,
Time 10000 hour
250 MPa

@Temperature 550 °C,
Time 3.60e+7 sec
36300 psi

@Temperature 1020 °F,
Time 10000 hour
Modulus of Elasticity 200 GPa
29000 ksi
RT
120 GPa

@Temperature 1000 °C
17400 ksi

@Temperature 1830 °F
163 GPa

@Temperature 500 °C
23600 ksi

@Temperature 932 °F
Thermal Properties Metric English Comments
CTE, linear 18.2 µm/m-°C

@Temperature 500 °C
10.1 µin/in-°F

@Temperature 932 °F
19.5 µm/m-°C

@Temperature 1000 °C
10.8 µin/in-°F

@Temperature 1830 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
0.580 J/g-°C

@Temperature 500 °C
0.139 BTU/lb-°F

@Temperature 932 °F
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
21.2 W/m-K

@Temperature 500 °C
147 BTU-in/hr-ft²-°F

@Temperature 932 °F
29.0 W/m-K

@Temperature 1000 °C
201 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Maximum Service Temperature, Air 1000 °C
1830 °F
Dry Air
Component Elements Properties Metric English Comments
Carbon, C 0.050 %
0.050 %
Cerium, Ce 1.3 %
1.3 %
Chromium, Cr 18.5 %
18.5 %
Iron, Fe 69.2 %
69.2 %
Nickel, Ni 9.5 %
9.5 %
Nitrogen, N 0.15 %
0.15 %
Silicon, Si 1.3 %
1.3 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000840 ohm-cm
0.0000840 ohm-cm
RT
Processing Properties Metric English Comments
Annealing Temperature 900 °C
1650 °F
Stress Relief Annealing (min. 0.5 h)
1020 - 1120 °C
1870 - 2050 °F
Solution Annealing