- Solvay TECHNYL® A 218G1 V25 Black 34N PA66, 25% glass fiber, DRY
Solvay TECHNYL® A 218G1 V25 Black 34N PA66, 25% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218G1 V25 Black 34N PA66, 25% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 25% of glass fiber, for injection molding. This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. Available in: Europe and North AmericaProduct Applications: TECHNYL® A 218G1 V25 BLACK 34N is particularly recommended for the injection molding of parts in permanent contact with cooling liquids in cars, such as: - cooling and heating radiator systems, header tanks, thermostat components, inlet / outlet pipes. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183/A |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec |
0.90 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 Type 1A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Tensile Modulus | 8.40 GPa | 1220 ksi | ISO 527 Type 1A |
| Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
| Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 6.80 J/cm² | 32.4 ft-lb/in² | ISO 179/1eU |
| 5.00 J/cm² @Temperature 120 °C, Time 720000 sec |
23.8 ft-lb/in² @Temperature 248 °F, Time 200 hour |
after aging water/glycol; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
15.0 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 350 V | 350 V | Solution A; IEC 60112 |
| 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Crastin® SK615SF BK591 PBT (Unverified Data**)
- SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific)
- Polyram Polytron P50B11 Homopolymer Polypropylene, Chemically Coupled 50% LGF
- Fainplast Compounds HL 91 Flexible PVC, Insulation for High Temperatures
- Arlon 920-10CxxFR-P1 0.020" Self-Fusing Silicone Rubber Tape
- ExxonMobil Escorene® LL-8361 LMDPE Rotational Molding Grade (discontinued **)
- DuPont Performance Polymers Zytel® HTN FE8200 NC010 Polyphthalamide (PPA) (Unverified Data**)
- SABIC Innovative Plastics NORYL FE1740PW PPE+PS (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved