NOVA Chemicals Novapol® PF-0218-D Butene LLDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film |
| Manufacturer | NOVA Chemicals |
| Trade Name | Novapol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Novapol® PF-0218-D Butene LLDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: High MI for easier extrusion.Applications: Trash bags, bags-on-roll, garment film.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Break, MD | 690 % | 690 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Coefficient of Friction | <= 0.20 | <= 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.50 g/micron | 88.9 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 10.6 g/micron | 269 g/mil | ASTM D1922 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 20 % @Thickness 0.0250 mm |
20 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 35 % | 35 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 195 - 205 °C | 383 - 401 °F |
Users viewing this material also viewed the following:
- NextGen Adhesives P907-01 Fiber Optic Adhesive
- SABIC Innovative Plastics Extem UH1016M TPI Blend
- Overview of materials for Polychlorotrifluoroethylene; Molded
- LG Chemical LUMAX GP-5200 General Purpose PBT, 20 % Polymer Alloy
- Lord Adhesives 8300 Medium Setting, Medium Viscosity Ethyl Cyanoacrylate Adhesive
- Solvay TECHNYL® C 538XT V30 Natural W PA6, 30% glass filled, DRY
- Techmer ES HiFill® PA6 GB20 L 20% Glass Bead Filled
- 3M 425 EMI Shielding Tape
- 3M 466XL Extended Liner Tapes
- BASF Ultramid® B3GM35 Q611 15/25% Glass/Mineral Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved