- Solvay TECHNYL® A 218 V40 PA66, 40% glass fiber, DRY
Solvay TECHNYL® A 218 V40 PA66, 40% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 V40 PA66, 40% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA66, reinforced with 40% of glass fiber, heat stabilized for injection molding.Available in: Asia Pacific, Europe and North AmericaProduct Applications: TECHNYL A 218 V40 is used in all sectors of industry, offering and excellent combination between thermal and mechanical properties. This grade is used in: automotive industry, manufacture of components for electrical tools, and transport and building. This product is available in natural and black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183/A |
| Water Absorption | 0.70 % @Temperature 23.0 °C, Time 86400 sec |
0.70 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0057 cm/cm | 0.0057 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 225 MPa | 32600 psi | ISO 527 Type 1A |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527 Type 1A |
| Flexural Modulus | 10.8 GPa | 1570 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 13.5 kJ/m² | 6.42 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 9.70 J/cm² | 46.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 280 °C | 500 - 536 °F | |
| Front Barrel Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-300°C |
Users viewing this material also viewed the following:
- Petromont 8001 High Density Polyethylene Resin
- Global PP-2800-J Polypropylene Block Copolymer
- SCG Chemicals EL-Leneâ„¢ LD1905FA Low Density Polyethylene Film
- A. Schulman POLYBATCH™ Lattice Green 30155U Concentrate Based In LLDPE
- DuPont Teijin Films Teijin® Tetoron® S Polyester Film, 300 Gauge
- Braskem CP 401 HC Injection Molding Polypropylene
- Braskem LL3800N HDPE Cast Film Extrusion Polyethylene Copolymer
- Arlon 56586R026 0.027" (0.686 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Dow Corning 2-9034 EMULSION
Copyright © lookpolymers.com All Rights Reserved