- HOME
- POLYMER SEARCH
- Renewable/Recycled Polymer
- Metabolix Mirelâ„¢ P1004 Injection Molding Grade PHA Bioplastic
Metabolix Mirelâ„¢ P1004 Injection Molding Grade PHA Bioplastic
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | Metabolix |
| Trade Name | Mirel™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Metabolix Mirelâ„¢ P1004 Injection Molding Grade PHA Bioplastic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mirel P1004 is a general purpose injection molding grade with high toughness.About Mirel BioplasticsMirel is a family of bioplastic materials that have physical properties comparable to petroleum-based resins, yet are both biobased and biodegradable in natural soil and water environments, home composting systems, and industrial composting facilities, where these facilities are available. The rate and extent of Mirel's biodegradablility will depend on the size and shape of the articles made from it. However, like nearly all bioplastics and organic matter, Mirel is not designed to biodegrade in conventional landfills.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0125 - 0.0155 cm/cm | 0.0125 - 0.0155 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 24.0 MPa | 3480 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Flexural Strength | 33.0 MPa | 4790 psi | ASTM D790 A |
| Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 A |
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 B |
| Deflection Temperature at 1.8 MPa (264 psi) | 36.0 °C | 96.8 °F | ASTM D648 B |
| Vicat Softening Point | 124 °C | 255 °F | ASTM 1525 B10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 175 - 180 °C | 347 - 356 °F | Reverse Temperature Profile |
| Middle Barrel Temperature | 170 - 175 °C | 338 - 347 °F | |
| Front Barrel Temperature | 165 - 170 °C | 329 - 338 °F | |
| Nozzle Temperature | 165 - 170 °C | 329 - 338 °F | |
| Melt Temperature | 160 - 165 °C | 320 - 329 °F | |
| Mold Temperature | 55.0 - 65.0 °C | 131 - 149 °F | (A/B) |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Desiccant |
| Back Pressure | <= 3.45 MPa | <= 500 psi | Low |
| Screw Speed | <= 200 rpm | <= 200 rpm | Slow |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 2nd Stage Pressure | <30% | of 1st Stage Pressure (Low) |
| Equipment Recommendation: Non-Return Valve | Standard Check Ring | |
| Equipment recommendation: Screw Profile | 2.2:1 to 2.6:1 | Low Shear GP |
Users viewing this material also viewed the following:
- RheTech Products FRP300-00 20% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Natural
- MV Labs RU460 K2RuCl6 Potassium hexachlororuthenate(IV)
- Okulen® 2000 PE-UHMW, GB
- LyondellBasell Petrothene® GA601032 Linear Low Density Polyethylene
- Glastic Laminates/Shapes SG-200 Fiberglass-Reinforced Polyester Rod
- Zylog Hipolyene® 2530 DW Thermoplastic Polyolefin & PP Compound
- Teknor Apex Telcar® TL-87-L832-E Thermoplastic Elastomer
- Dow Corning SYL-OFF® PMCPSL 9176 Anchorage Additive
- Dymax 9-911 Strain Relief, Wire and Parts Tacking Adhesive
- A. Schulman SCHULAMID® E-17222 High Impact Nylon 66
Copyright © lookpolymers.com All Rights Reserved