Solvay TECHNYL® A 218 MT15 V 25 Black 21N PA66, 25/15% glass/mineral fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 MT15 V 25 Black 21N PA66, 25/15% glass/mineral fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 25% of glass fiber and 15% of mineral filler, heat stabilized, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® A 218 MT15 V25 is recommended in all industrial parts, offering a good combination between thermal and mechanical properties. This grade is commonly used in the automotive industry to mould large parts with a low warpage, such as: rocker cover, car body parts, engine covers. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183/A |
| Water Absorption | 1.4 % @Temperature 23.0 °C, Time 86400 sec |
1.4 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0054 cm/cm | 0.0054 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527 Type 1A |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 Type 1A |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+14 ohm-cm | 3.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 5.00e+13 ohm | 5.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 425 V | 425 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 265 °C | 500 - 509 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® V-341 Polybutadiene Prepreg, 503 Quartz Reinforced
- Nitriflex N-7410 NBR / PVC
- Lubriplate Synthetic Worm Gear Lubricant Specialty Oil and Fluid
- Heatbath/Park Carbo Fluid D Carburizer
- Techmer ES HiFill® TPU/E 0140
- A. Schulman POLYBATCH™ Dark Grey LL80362/4 Concentrate Based In LLDPE
- ExxonMobil Escorene® LD 755.CM Molding, extrusion and compounding resin
- 3M Highland™ 3565 Label Protection Tape
- PolyChem Alloy PolySept 2006
Copyright © lookpolymers.com All Rights Reserved