Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 30% of glass spheres, for injection molding.Available in: EuropeProduct Applications: TECHNYL® A 216 S30 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is recommended for mechanical components which require a very good surface finish with low warpage, and good compression strength. This product is available in natural, black, grey, red, white, and in special colors on requestInformation provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Water Absorption | 0.75 % @Temperature 23.0 °C, Time 86400 sec |
0.75 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | |
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 type 1 A |
| Elongation at Break | 9.0 % | 9.0 % | ISO 527 Type 1A |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 Type 1A |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| Flexural Modulus | 3.85 GPa | 558 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² | 1.19 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C @Temperature 23.0 - 85.0 °C |
3.33 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+13 ohm-cm | 5.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 5.00e+13 ohm | 5.00e+13 ohm | IEC 60093 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Lucite International Colacryl ® TS1742 Acrylic Dental Resin
- Seals Eastern 5053 Ethylene-Propylene Rubber
- Daikin POLYFLON M-112 PTFE Molding Powder, Fine Cut
- Chi Mei Kibilac® PW-997S ASA Polymer
- Asahi Kasei ASACLEAN EX Purging Compound
- 3M Scotch-Weld™ AC77 Instant Adhesive Primer
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 60 PHR N330 (HAF) Black
- Ashley Polymers Ashlene® RH180 Acetal
- DuPont Performance Polymers Rynite® 935 NC010 PET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved