Arkema Group Pebax® 6333 Polyether Block Amide (PEBA)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyether Block Amide (PEBA) |
| Manufacturer | Arkema |
| Trade Name | Pebax® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Pebax® 6333 Polyether Block Amide (PEBA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | 24 hr in water at 20°C; ASTM D570 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | 20°C and 65% RH; ASTM D570 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ASTM D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 440 % | 440 % | ASTM D638 |
| Elongation at Yield | 20 % | 20 % | ASTM D638 |
| Modulus of Elasticity | 0.260 GPa | 37.7 ksi | ASTM D638 |
| Flexural Modulus | 0.290 GPa | 42.1 ksi | ASTM D790 |
| Resilience | 0.56 | 0.56 | BS 903 par: A 8 |
| Flex Crack Resistance | 5.0 | 5.0 | [mm] 20°C / 100000 flexures; ASTM D813 |
| 14 | 14 | [mm] -20°C / 50000 flexures; ASTM D813 | |
| Izod Impact, Notched | NB | NB | ASTM D256-A |
| 1.00 J/cm @Temperature -40.0 °C |
1.87 ft-lb/in @Temperature -40.0 °F |
ASTM D256-A | |
| Izod Impact, Unnotched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Tear Strength | 150 kN/m | 856 pli | notched; ASTM D624 (C) |
| 168 kN/m | 959 pli | unnotched; ASTM D624 (C) | |
| Taber Abrasion, mg/1000 Cycles | 46 | 46 | ASTM D1242 |
| Abrasion | 34 | 34 | mm<sup>3</sup>; DIN 53516 |
| Compression Set | 5.0 % | 5.0 % | Load = 9.3 MPa (22 hr / 70°C); ASTM D395 Method A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 33.0 J/g | 14.2 BTU/lb | ASTM D3417 |
| CTE, linear | 140 µm/m-°C @Temperature -40.0 - 140 °C |
77.8 µin/in-°F @Temperature -40.0 - 284 °F |
ASTM D696 |
| Melting Point | 169 °C | 336 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Vicat Softening Point | 161 °C | 322 °F | under 1 daN; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+13 ohm @Temperature 20.0 °C |
1.00e+13 ohm @Temperature 68.0 °F |
65% RH; ASTM D257 |
Users viewing this material also viewed the following:
- Hong Kun Group UV 360 UV Absorber
- LATI Latigea B01 I8 Bio-Polymer
- Spartech M60480 General Purpose PVC
- Spartech Royalite R66 PVC/Acrylic Fire Rated Sheet
- SABIC Innovative Plastics LNP THERMOCOMP JF004RXP PES (Europe-Africa-Middle East)
- Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade
- Zoltek Panex 35® Tow Weave Carbon Fiber Fabrics
- 3M Cushion-Mount™ E1715 Plus Plate Mounting Tapes with Easy Mount Adhesive
- Elisto THERMOSTAR® LC 6000 Insulation Material
Copyright © lookpolymers.com All Rights Reserved