- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Sax Polymers SAXLAC 310A Acrylonitrile Butadiene Styrene
Sax Polymers SAXLAC 310A Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Sax Polymers |
| Trade Name | SAXLAC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXLAC 310A Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Saxalac 310A is a medium viscosity, impact resistant ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 50.0 MPa | 7250 psi | ISO 527-1 |
| Elongation at Break | 10 % | 10 % | ISO 527-1 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 9.20 J/cm² @Temperature -30.0 °C |
43.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 95.0 °C @Thickness 2.00 mm |
203 °F @Thickness 0.0787 in |
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 98.0 °C | 208 °F | 50B; ISO 306 |
| Glow Wire Test | 650 °C | 1200 °F | IE/CEN 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 925A PC (Asia Pacific)
- Dow Isoplast® 302 Polyurethane (PUR-RT), Clear Amorphous Polymer (discontinued **)
- MetaFoam Copper-Silver Foam
- SABIC Innovative Plastics LNP LUBRICOMP YL003 Polyester Elastomer (Europe-Africa-Middle East)
- Borealis Daploy™ WB135HMS High Melt Strength Polypropylene for Foam Extrusion
- Topas Advanced Polymers TOPAS® 5013S-04 Cyclic Olefin Copolymer (COC)
- Dow SiLK™ I 360 Semiconductor Dielectric Resin
- A. Schulman ComAlloy Hiloy® 432 Glass Reinforced, PBT Alloy
- Arkema Group KYNAR® 460 Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
- Panjin Zhongrun Chemerize 085G Low Viscosity CoPEEK
Copyright © lookpolymers.com All Rights Reserved