Samyang Trirex® 3025N1 Polycarbonate, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® 3025N1 Polycarbonate, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries.Characteristics:Medium viscositySelf ExtinguishingApplications:1/16 inch UL V-0All information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 11 g/10 min @Load 1.20 kg, Temperature 300 °C |
11 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 66.7 MPa | 9670 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Yield Strength | 87.3 MPa | 12700 psi | ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | ASTM D790 |
| Izod Impact, Unnotched | 7.35 J/cm @Thickness 3.17 mm |
13.8 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C | 30.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dissipation Factor | 0.0082 @Frequency 1.00e+6 Hz |
0.0082 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 90 sec | 90 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Middle Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Front Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Melt Temperature | 300 - 310 °C | 572 - 590 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD163R PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP DX07350 PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend (Asia Pacific)
- A. Schulman POLYBATCH™ Blue 4535 Concentrate Based In Polyethylene
- Daikin POLYFLON MG-1431F PTFE 20% Glass Fiber and 5% MoS2 Filled Molding Powder, High Apparent Density, Free Flow
- Fainplast Compounds HL 92/1 Flexible PVC, Insulation for High Temperatures
- Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Conditioned)
- Aremco Aremco-Bond™ 2335 Ultra High Temperature Epoxy
- Lubrizol Advanced Materials Pearlstick® 46-73/27 Polyester based TPU (discontinued **)
Copyright © lookpolymers.com All Rights Reserved