A. Schulman ComAlloy® E-12812 Easy Flow Glass Reinforced Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman ComAlloy® E-12812 Easy Flow Glass Reinforced Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Linear Mold Shrinkage 0.0090 cm/cm

@Thickness 3.175 mm
 0.0090 in/in

@Thickness 0.1250 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 99.3 MPa
14400 psi
ASTM D638
Elongation at Break 7.0 %
7.0 %
ASTM D638
Flexural Strength 161 MPa
23300 psi
ASTM D790
Flexural Modulus 4.82 GPa
699 ksi
ASTM D790
Izod Impact, Notched 0.427 J/cm
0.800 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.06 J/cm
7.60 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 219 °C
426 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 203 °C
397 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 2 - 4 hour
2 - 4 hour
Predrying