Adamas Adalon® 237 PTFE, 25% Glass Fiber
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 237 PTFE, 25% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.23 - 2.25 g/cc | 2.23 - 2.25 g/cc | ASTM D792 |
| Deformation | 5.0 - 6.5 % | 5.0 - 6.5 % | Permanent deformation after 24 hrs @ 23°C; ASTM D621 |
| 9.0 - 11 % | 9.0 - 11 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 54 - 58 | 54 - 58 | ASTM D2240 |
| Ball Indentation Hardness | 50.0 - 55.0 MPa | 7250 - 7980 psi | ISO 2032-N132 |
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ASTM D4894 |
| Elongation at Break | >= 160 % | >= 160 % | ASTM D4894 |
| Compressive Strength | 0.785 - 0.883 MPa @Temperature 23.0 °C, Time 86400 sec |
114 - 128 psi @Temperature 73.4 °F, Time 24.0 hour |
@ 1% deformation, 140 Kg/cm<sup>2</sup>; ASTM D621 |
| Coefficient of Friction, Dynamic | 0.15 - 0.17 | 0.15 - 0.17 | ASTM D1894 |
| Coefficient of Friction, Static | 0.17 - 0.19 | 0.17 - 0.19 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 260 °C | 500 °F | DSC |
| Minimum Service Temperature, Air | -180 °C | -292 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Gouda Vuurvast ADHESIET A Dry Air-Setting Refractory Mortar
- LG Chemical Lupoy 1320C-07 Polycarbonate Resin
- Karina 6148/1-RTR Kariprene Black
- A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
- A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
- Elgiloy® Co-Cr-Ni Alloy, Wire, 30% Cold Reduction, Heat Treated
- BASF Ultramid® A3EG7 35% Glass Filled PA66 (Conditioned)
- Anderman Ceramics EREC99 Cerium Oxide
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Non-Black, Precipitated Calcium Carbonate
- Sumitomo Bakelite North America FM 3000 Cellulose Reinforced Phenolic Novolac
Copyright © lookpolymers.com All Rights Reserved