| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PS-15GB/15T Polybutylene Terephthalate (PBT), Glass Bead Filled, PTFE Lubricated
(discont.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Bead FilledPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.83 GPa | 410 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 77.2 MPa | 11200 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.347 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.650 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 266 °C | 460 - 510 °F | Molding |
| Mold Temperature | 54.4 - 93.3 °C | 130 - 200 °F | |
| Drying Temperature | 104 °C | 220 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT NN-30LCF/002 Grey Polyamide 66 (Nylon 66)
- Solvay Specialty Polymers Veradel® 3500 Polyethersulfone (PESU)
- Total PPH 7062 Polypropylene, Homopolymer
- Unitika FUN-8000
- Cytec Conathane® CC-1195 (Conap) Polyurethane Two-component Dielectric Conformal Coating
- E-Polymers TEKAMID® TA210ST Super Tough PA66, DAM
- A. Schulman ComAlloy Hiloy® 617 Nylon 6, Glass/Mineral Reinforced, UL
- SABIC Innovative Plastics Lexan® ML6230 PC Copolymer
- RheTech Products HP501-00 High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
Copyright © lookpolymers.com All Rights Reserved