SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+Polyester, UV Stabilized, Transparent
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.050 %
0.050 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D1238
Melt Index of Compound 15 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 73
73
10S reading; ASTM D2240
Tensile Strength at Break 46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D638
54.0 MPa
7830 psi
50 mm/min; ISO 527
Tensile Strength, Yield 47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Elongation at Break 150 %
150 %
Type I, 50 mm/min; ASTM D638
>= 200 %
>= 200 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
>= 5.0 %
>= 5.0 %
50 mm/min; ISO 527
Tensile Modulus 1.52 GPa
220 ksi
50 mm/min; ASTM D638
1.60 GPa
232 ksi
1 mm/min; ISO 527
Flexural Strength 78.0 MPa
11300 psi
2 mm/min; ISO 178
Flexural Yield Strength 71.0 MPa
10300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.68 GPa
244 ksi
1.3 mm/min, 50 mm span; ASTM D790
1.70 GPa
247 ksi
2 mm/min; ISO 178
Izod Impact, Notched 11.2 J/cm
21.0 ft-lb/in
ASTM D256
0.730 J/cm

@Temperature -30.0 °C
 1.37 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -10.0 °C
 2.38 ft-lb/in²

@Temperature 14.0 °F
 80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 95.0 J

@Temperature 23.0 °C
 70.1 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
105 µm/m-°C

@Temperature -40.0 - 40.0 °C
 58.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
105 µm/m-°C

@Temperature -40.0 - 40.0 °C
 58.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
105 µm/m-°C

@Temperature -40.0 - 40.0 °C
 58.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
105 µm/m-°C

@Temperature -40.0 - 40.0 °C
 58.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 85.0 °C
<= 185 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 79.0 °C

@Thickness 3.20 mm
 174 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
80.0 °C
176 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
75.0 °C

@Thickness 3.20 mm
 167 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 91.0 °C
196 °F
Rate B/50; ASTM D1525
96.0 °C
205 °F
Rate B/120; ISO 306
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
 UL 94
Glow Wire Test 750 °C

@Thickness 1.00 mm
 1380 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Optical Properties Metric English Comments
Refractive Index 1.539
1.539
ISO 489
Haze 1.0 %

@Thickness 2.54 mm
 1.0 %

@Thickness 0.100 in
 ASTM D1003
Transmission, Visible 88 %
88 %
2.54 mm; ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D257
Comparative Tracking Index >= 600 V
>= 600 V
UL 746A