- SABIC Innovative Plastics Valox® VX4910 ASA+PBT (Europe-Africa-Middle East)
SABIC Innovative Plastics Valox® VX4910 ASA+PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® VX4910 ASA+PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ASTM D229 |
| Viscosity | 160000 cP | 160000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 20 g/10 min @Load 3.80 kg, Temperature 200 °C |
20 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D1238 |
| 40 g/10 min @Load 5.00 kg, Temperature 265 °C |
40 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 | |
| Melt Index of Compound | 25 g/10 min @Load 5.00 kg, Temperature 250 °C |
25 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 35 g/10 min @Load 5.00 kg, Temperature 265 °C |
35 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
| Hardness, H358/30 | 100 MPa | 14500 psi | ISO 2039-1 |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| 4.0 % | 4.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.60 GPa | 667 ksi | 5 mm/min; ASTM D638 |
| 4.60 GPa | 667 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 115 MPa | 16700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 115 MPa | 16700 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 115 MPa | 16700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 120 MPa | 17400 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.40 GPa | 493 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.80 GPa | 551 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.550 J/cm | 1.03 ft-lb/in | ASTM D256 |
| 0.450 J/cm @Temperature -30.0 °C |
0.843 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 0.500 J/cm @Temperature 0.000 °C |
0.937 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 4.40 J/cm | 8.24 ft-lb/in | ASTM D4812 |
| 3.40 J/cm @Temperature -30.0 °C |
6.37 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature 0.000 °C |
2.38 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/2C |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/2C |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Dart Drop, Total Energy | 45.0 J @Temperature 23.0 °C |
33.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.7 µm/m-°C @Temperature 23.0 - 150 °C |
19.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 41.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| 50.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 81.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 120 µm/m-°C @Temperature 23.0 - 60.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| 196 µm/m-°C @Temperature 23.0 - 150 °C |
109 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 150 °C | 302 °F | Rate B/50; ASTM D1525 |
| 150 °C | 302 °F | Rate B/50; ISO 306 | |
| 155 °C | 311 °F | Rate B/120; ISO 306 | |
| 218 °C | 424 °F | Rate A/50; ISO 306 | |
| 218 °C | 424 °F | Rate A/50; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 66-43GF 43% Glass Fiber Filled Nylon 66 for Injection Molding
- Parabeam Industrie Paraglass 12 3D Glass Fabric
- ExxonMobil Escorene® LD-708 EVA Film Resin (discontinued **)
- Lubriplate Vacuum Pump Oil Specialty Oil and Fluid
- Haynes 556® alloy, bar after 16000 hours at 537°C
- Samsung Cheil Industries Starex® BF-0677HF MABS, Unreinforced Scratch Resistant
- SABIC Innovative Plastics LNP THERMOCOMP RX12402 PA 66
- Tra-Con Tra-Duct 926K01 Long Work Life Flexible Silver-Filled Epoxy Adhesive
- DSM Arnitel® UM552 Polyether Ester Elastomer (European Grade)
- Aclo Accutech Polypropylene Copolymer CP0436G20CL Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved