SABIC Innovative Plastics LNP THERMOCOMP RF0069SZ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF0069SZ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF0069SZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of th is grade include: Flame Retardant, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.67 g/cc | 1.67 g/cc | ASTM D792 |
| Density | 1.66 g/cc | 0.0600 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.790 % | 0.790 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 157 MPa | 22800 psi | Type I, 5 mm/min; ASTM D638 |
| 157 MPa | 22800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.82 GPa | 1859 ksi | 1 mm/min; ISO 527 |
| 12.84 GPa | 1862 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 217 MPa | 31500 psi | ISO 178 |
| 221 MPa | 32100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 11.03 GPa | 1600 ksi | 2 mm/min; ISO 178 |
| 11.4 GPa | 1650 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 231 °C @Thickness 3.20 mm |
448 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- IBC Advanced Alloys C17510 Beryllium Copper Alloy Rounds, Temper A(TB00)
- Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened
- Solvay TECHNYL® C 216 PA6, Conditioned
- SABIC Innovative Plastics LNP LUBRILOY UA200A PPA (Asia Pacific)
- Solvay MACKADET® EQ-112 Surfactant
- Universal Wire Works 347 Stainless Steel (AMS 5680) Filler Metal
- Du-Co Ceramics S-570 Silica
- Arlon CP-434R Bulk Compound
- BASF Petra® 130 FR BK-112 30% Glass Filled PET
- 3M Scotchgard™ Resilient Floor Protector
Copyright © lookpolymers.com All Rights Reserved