SABIC Innovative Plastics Valox® V3903WX PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® V3903WX PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced fllame retardant PBT/PC blends with good chemical resistance and low temperature impact, UV stablized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Water Absorption at Saturation | 0.010 % | 0.010 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 0.750 - 2.30 mm |
0.0080 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0086 cm/cm @Thickness 0.750 - 2.30 mm |
0.0086 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 7.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 13 g/10 min @Load 5.00 kg, Temperature 265 °C |
13 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 80 % | 80 % | Type I, 50 mm/min; ASTM D638 |
| 89 % | 89 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.00 GPa | 290 ksi | 50 mm/min; ASTM D638 |
| 2.05 GPa | 297 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 74.0 MPa | 10700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.91 GPa | 277 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.20 GPa | 464 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.90 J/cm | 14.8 ft-lb/in | ASTM D256 |
| 2.20 J/cm @Temperature -30.0 °C |
4.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 2.60 J/cm @Temperature -20.0 °C |
4.87 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| 4.90 J/cm @Temperature -10.0 °C |
9.18 ft-lb/in @Temperature 14.0 °F |
ASTM D256 | |
| 6.00 J/cm @Temperature 0.000 °C |
11.2 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*3; ISO 180/1A |
| 20.0 kJ/m² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| 58.0 kJ/m² @Temperature 0.000 °C |
27.6 ft-lb/in² @Temperature 32.0 °F |
80*10*3; ISO 180/1A | |
| Charpy Impact, Notched | 5.40 J/cm² | 25.7 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.80 J/cm² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 85.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 85.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 96.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 98.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C @Thickness 3.20 mm |
235 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 96.0 °C @Thickness 6.40 mm |
205 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 117 °C | 243 °F | Rate B/50; ISO 306 |
| 120 °C | 248 °F | Rate B/120; ISO 306 | |
| 120 °C | 248 °F | Rate B/50; ASTM D1525 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| 175 - 250 V | 175 - 250 V | UL 746A |
Users viewing this material also viewed the following:
- Nye Lubricants 750A (IG) Synthetic Oil
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 5.0 PHR Wacker HDK N20 Filler
- MetalTek IN® 909 Centri-Vac Nickel Cobalt Based Alloy
- Greene Tweed Fluoroelastomer 742 FKM
- Lanxess Durethan® BKV 50 H EF DUS022 900116 Nylon 6, Glass Fiber Reinforced
- Materion Brush 1915â„¢ Heat Treated Temper Wire, 0.375" - 0.500"
- Hexion UP 802 Unsaturated Polyester Resin, High Surface Quality, Low Shrinkage, High Arc Resistance
- Struktol V-MAT G Processing Additive, Matting Agent
- A. Schulman POLYFLAM™ CFP 4611 11% CACO3 filled copolymer polypropylene product
- Cheng Yu Plastic SW02 POM/PTFE
Copyright © lookpolymers.com All Rights Reserved