Polymer Property : Flexural Strength = 12500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
PolyOne Geon™ Vinyl Rigid Extrusion 84110 Polyvinyl Chloride, Rigid (PVC, Rigid) Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this product. Note: The Cell Classification was determined using the notched Izod te..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
PolyOne Geon™ Vinyl Rigid Extrusion 87560 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Flexural Strength	86.0 MPa	12500 psi	ASTM D790
Plaskolite West Optix® CA-924 Impact Modified Acrylic Resin Injection Molding Grade Pellets. Good impact strength.
Flexural Strength	<= 86.0 MPa	<= 12500 psi	ISO 178
Polykemi AB POLYasa 2008F UV-stabilized, High Flow ASA Information provided by Polykemi AB
Flexural Strength	86.0 MPa	12500 psi	ISO 178
SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS (Europe-Africa-Middle East) LNP* Faradex* NS003 is a compound based on PC+ABS Blend resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
Flexural Strength	86.0 MPa	12500 psi	10mm/min; ASTM D790
Qualchem Danaprop PP2GF-15 Polypropylene, 15% Glass Fiber Polypropylene (homo-polymer) reinforced with glass fiberInformation provided by Qualchem Zrt.
Flexural Strength	86.2 MPa	12500 psi	ASTM D790-1
Premix Premi-Glas® 8102-20 Glass Reinforced Polyester BMC  (discontinued **) Description: Premi-Glas® 8102-20 is a glass reinforced thermoset polyester Bulk Molding Compound designed for injection molding of automotive forward lighting reflectors. Key features and benefits:..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
I. Stern WC-102 General Purpose Crystal Polystyrene Features:Good Processing CharacteristicsUL Classification 94 HBExcellent Water ClarityComplies with FDA Title 21 CFR 177.1640ApplicationsExtrusion FoamDisplaysInformation provided by I. Stern & Co. ..
Flexural Strength	86.0 MPa	12500 psi
Haysite 14100 Polyester BMC, 15% Glass Reinforced The 14100 series bulk molding compound is an electrical grade material that can be compression, transfer, or injection molded. Offering good mechanical strength and excellent electrical properties, ..
Flexural Strength	86.0 MPa	12500 psi	ASTM D790
LG Chemical LUPOL LW-4407 Low Warpage Polypropylene, 40% Glass Fiber/Mineral Filler Reinforced, Heat Resistant LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
Flexural Strength	86.0 MPa	12500 psi	ISO 178
SABIC Innovative Plastics LNP LUBRILOY D2000P PC (Asia Pacific) LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing.
Flexural Strength	86.0 MPa	12500 psi	ISO 178
Styrolution PS 165 N/L GPPS Styrolution PS 165N/L is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.High molecular weightGood flow characteristicsAppropriate for blending with HIPS..
Flexural Strength	86.0 MPa	12500 psi	ISO 178
SABIC Innovative Plastics LNP THERMOTUF VF1001S Super Tough Nylon LNP* Thermotuf* VF1001S is a Super Tough Nylon containing glass fiber. Characteristics of this grade is Heat Stabilized.
Flexural Strength	86.0 MPa	12500 psi	ASTM D790
Plenco 5482 Phenolic, Granular, Transfer Molded PLENCO 05482 is an organic reinforced phenolic molding compound formulated with graphite to improve the abrasion resistance. 05482 is available in black and brown. 05482 is not recommended for elect..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman.
Flexural Strength	86.0 MPa	12500 psi	ISO 178
Denka MALECCA K-400 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Ensinger Tecatron® XP-64B Compression Molded PPS Compound, 40% Fiberglass, Black Pigmented Ensinger Special Polymers has over twenty different grades of TECATRON PPS available. Custom formulations can be blended to suit specific applications. Compression molding is amenable to short run p..
Flexural Strength	86.0 MPa	12500 psi	chs 0.05 in/min; SL 2 inches; ASTM D790
Diamond Polymers NPP25-0303 GF20 20% Glass Filled Polypropylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Ensinger Tecast Vekton™ 6PAG Graphite-Filled Cast Nylon 6 (PA6) Tecast® 6PAG is a graphite powder-filled with properties similar to MoS2-filled but better suited to wet applications.General Tecast® Cast Nylon Information: Tecast cast nylon, available in a vari..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Ensinger Tecast Vekton™ 6PAM MoS2-Filled Cast Nylon 6 (PA6) Tecast® 6PAM is a molybdenum disulfide-filled cast nylon 6 used for general bearings and wear applications and for its superior strength and hardness.General Tecast® Cast Nylon Information: Tecast..
Flexural Strength	86.2 MPa	12500 psi	ASTM D-790
Axiall Tuf-Stif 2804 Rigid PVC, Extrusion Georgia Gulf Tuf-Stif 2804 is a special purpose rigid PVC profile extrusion compound designed for applications requiring the following properties: Improved toughness as compared to Tuf-StiffRigidit..