SABIC Innovative Plastics Valox® V3500EX PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® V3500EX PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unfilled PBT,Flame Retardant, good flow, high elongation at break for Extrusion applications (Monofilaments, Insulation Cables),Electrical Parts and Connectors
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
ASTM D792
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Viscosity 170000 cP
170000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.011 - 0.018 cm/cm
0.011 - 0.018 in/in
on Tensile Bar; SABIC Method
Linear Mold Shrinkage, Transverse 0.0090 - 0.018 cm/cm
0.0090 - 0.018 in/in
on Tensile Bar; SABIC Method
Melt Flow 50 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 50 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 ASTM D1238
50 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 50 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 13 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
13 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 13 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
40 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 40 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ISO 2039-2
Hardness, H358/30 170 MPa
24700 psi
ISO 2039-1
Tensile Strength at Break 40.0 MPa
5800 psi
Type I, 50 mm/min; ASTM D638
50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Elongation at Break 15 %
15 %
Type I, 50 mm/min; ASTM D638
>= 70 %
>= 70 %
50 mm/min; ISO 527
Elongation at Yield 3.0 %
3.0 %
Type I, 50 mm/min; ASTM D638
3.0 %
3.0 %
50 mm/min; ISO 527
Tensile Modulus 3.10 GPa
450 ksi
50 mm/min; ASTM D638
3.20 GPa
464 ksi
1 mm/min; ISO 527
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
Flexural Modulus 2.85 GPa
413 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.400 J/cm
0.749 ft-lb/in
ASTM D256
0.400 J/cm

@Temperature 0.000 °C
 0.749 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
0.400 J/cm

@Temperature -30.0 °C
 0.749 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 9.50 J/cm
17.8 ft-lb/in
ASTM D4812
8.30 J/cm

@Temperature -30.0 °C
 15.5 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature 0.000 °C
 2.86 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 60.0 kJ/m²
28.6 ft-lb/in²
80*10*4; ISO 180/1U
60.0 kJ/m²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 9.50 J/cm²
45.2 ft-lb/in²
ISO 179/2C
8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²
2.86 ft-lb/in²
ISO 179/2C
0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
190 µm/m-°C

@Temperature 23.0 - 150 °C
 106 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
142 µm/m-°C

@Temperature 23.0 - 150 °C
 78.9 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
165 °C

@Thickness 3.20 mm
 329 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
80.0 °C

@Thickness 3.20 mm
 176 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 180 °C
356 °F
Rate B/50; ISO 306
180 °C
356 °F
Rate B/120; ISO 306
180 °C
356 °F
Rate B/50; ASTM D1525
220 °C
428 °F
Rate A/50; ISO 306
220 °C
428 °F
Rate A/50; ASTM D1525
UL RTI, Electrical 75.0 °C
167 °F
UL 746B
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 ASTM D150
2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 IEC 60250
Dielectric Strength 21.0 kV/mm

@Thickness 3.20 mm
 533 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
21.0 kV/mm

@Thickness 3.20 mm
 533 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
39.0 kV/mm

@Thickness 1.60 mm
 991 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
39.0 kV/mm

@Thickness 1.60 mm
 991 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
62.0 kV/mm

@Thickness 0.800 mm
 1570 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.016

@Frequency 1.00e+6 Hz
 0.016

@Frequency 1.00e+6 Hz
 ASTM D150
0.016

@Frequency 1.00e+6 Hz
 0.016

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 225 V
225 V
IEC 60112