Aclo Accutech Polypropylene Copolymer CP0437M30L Mica Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437M30L Mica Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Melt Flow | 16 g/10 min | 16 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 39 | 39 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ASTM D638 |
| Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
| Flexural Modulus | 2.100 GPa | 304.6 ksi | ASTM D790 |
| Izod Impact, Notched | 1.49 J/cm | 2.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.8 °C | 136 °F |
Users viewing this material also viewed the following:
- Radici Radilon® CA RV300L (cond.) Nylon 66/6
- Solvay Specialty Polymers Torlon® 4645 Polyamide-imide (PAI) (Unverified Data**)
- Gouda Vuurvast CURON 145 F Sp Dense Refractory Castable
- Lanxess Pocan® B 7425 000000 PBT, 20% Glass Spheres
- LG Chemical 25SPR GPPS
- A. Schulman FORMION™ FI 233 15% Mineral Reinforced Ionomer / Nylon Alloy
- Universal Wire Works BAg-7 (AMS 4763) Silver Brazing Filler Metal
- EMS-Grivory Grivory® GCL-3H anthracite PA*-CF30
- Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, Dry As Molded
- 3M 466XL Extended Liner Tapes
Copyright © lookpolymers.com All Rights Reserved