- Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler
- Lehmann & Voss LUVOCOM® 1301/CF/20 PPS, linear, with carbon fiber
Lehmann & Voss LUVOCOM® 1301/CF/20 PPS, linear, with carbon fiber
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301/CF/20 PPS, linear, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts with low creep.Electrically conductive, suitable for continuous discharging of statically generated electricity.Suitable for metall inserts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 |
| Water Absorption | <= 0.050 % | <= 0.050 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 180 MPa | 26100 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 17.0 GPa | 2470 ksi | |
| Flexural Strength | 250 MPa | 36300 psi | |
| Flexural Modulus | 16.0 GPa | 2320 ksi | |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | flatwise; ISO 179 1fU |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | |
| Coefficient of Friction, Static | 0.24 | 0.24 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft²-°F | HOT-DISK || 60x60x3 mm |
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Vicat Softening Point | 255 °C | 491 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF30-PA66 30% Long Carbon Fiber
- Radici Heraflex® E 7722 TPC-ET Thermoplastic Elastomer
- SABIC Innovative Plastics Lexan® ML6412 PC Copolymer (Asia Pacific)
- ExxonMobil Escorene® LL-3113 LLDPE/Hexene Premium High Strength 1.2 mil Film (discontinued **)
- Huntsman IROGRAN® CA116-205 TPU-Polyester
- Teknor Apex Telcar® TL EF-6177B-UV Thermoplastic Elastomer
- ChevronTexaco Bright-Cut® NM Metal Working Fluid
- Covestro Makrolon® 8345 Polycarbonate
- ExxonMobil Santoprene® 121-50E500 Thermoplastic Elastomer
- Diamond Polymers NPP25-0103 CF15 Conductive Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved