SABIC Innovative Plastics Valox® ENH4560 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® ENH4560 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* PBT resin.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ASTM D229 |
| Viscosity | 110000 cP | 110000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Melt Flow | 23 g/10 min @Load 5.00 kg, Temperature 265 °C |
23 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 |
| Melt Index of Compound | 16 g/10 min @Load 5.00 kg, Temperature 250 °C |
16 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
| Hardness, H358/30 | 142 MPa | 20600 psi | ISO 2039-1 |
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| 2.0 % | 2.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 5 mm/min; ASTM D638 |
| 11.0 GPa | 1600 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 170 MPa | 24700 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 170 MPa | 24700 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| 0.750 J/cm @Temperature 0.000 °C |
1.41 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.750 J/cm @Temperature -30.0 °C |
1.41 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D4812 |
| 5.00 J/cm @Temperature -30.0 °C |
9.37 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature 0.000 °C |
4.28 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| 37.0 kJ/m² @Temperature -30.0 °C |
17.6 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/2C |
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/2C |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 25.0 µm/m-°C @Temperature 23.0 - 150 °C |
13.9 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 150 µm/m-°C @Temperature 23.0 - 150 °C |
83.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 223 °C @Thickness 3.20 mm |
433 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 205 °C | 401 °F | Rate B/120; ISO 306 |
| 206 °C | 403 °F | Rate B/50; ISO 306 | |
| 207 °C | 405 °F | Rate B/50; ASTM D1525 | |
| 217 °C | 423 °F | Rate A/50; ASTM D1525 | |
| 220 °C | 428 °F | Rate A/50; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
| 22.0 kV/mm @Thickness 1.60 mm |
559 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 22.0 kV/mm @Thickness 1.60 mm |
559 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 32.0 kV/mm @Thickness 0.800 mm |
813 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| 32.0 kV/mm @Thickness 0.800 mm |
813 kV/in @Thickness 0.0315 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.14 @Frequency 1.00e+6 Hz |
0.14 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.14 @Frequency 1.00e+6 Hz |
0.14 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| 600 V | 600 V | IEC 60112 | |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- Total Lacqrene® 3351(EU) Impact Polystyrene (discontinued **)
- Lanxess Pocan® KU 1-7313 000000 PBT + PET, 15% Glass Fiber
- Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F)
- Teknor Apex Sarlink® 3440 Thermoplastic Elastomer
- ExxonMobil LLDPE LL 1001.32 Linear Low Density Polyethylene Resin
- BASF 3-Methoxypropylamine (MOPA)
- BASF Petra® 130 30% Glass Filled PET
- BASF Ultramid® 1403-2 NF3001 13% Glass Filled PA66 (Conditioned)
- ExxonMobil Escorene® LL-8361 LMDPE Rotational Molding Grade (discontinued **)
- EMS-Grivory Grivory® BM 20 SBG PA*
Copyright © lookpolymers.com All Rights Reserved