DuPont Teijin Films Melinex® 054 Polyester Film

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Melinex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Melinex® 054 Polyester Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Melinex® 054 is a high clarity, low balanced shrink polyester film which is two-side pretreated to promote adhesion to industrial coatings and inks.Information provided by DuPont.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 89.6 MPa
13000 psi
ASTM D882A
Film Tensile Strength at Yield, TD 89.6 MPa
13000 psi
ASTM D882A
Film Elongation at Break, MD 200 %
200 %
ASTM D882A
Film Elongation at Break, TD 120 %
120 %
ASTM D882A
Coefficient of Friction, Static 0.40 - 0.50
0.40 - 0.50
ASTM D1894
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
Film Tensile Strength at Break, TD 172 MPa
25000 psi
ASTM D882A
Thermal Properties Metric English Comments
Shrinkage, MD 1.0 %

@Temperature 190 °C,
Time 300 sec
1.0 %

@Temperature 374 °F,
Time 0.0833 hour
Unrestrained
Shrinkage, TD 0.80 %

@Temperature 190 °C,
Time 300 sec
0.80 %

@Temperature 374 °F,
Time 0.0833 hour
Unrestrained
Optical Properties Metric English Comments
Haze 0.30 %

@Thickness 0.0965 mm
0.30 %

@Thickness 0.00380 in
ASTM D1003
0.50 %

@Thickness 0.117 mm
0.50 %

@Thickness 0.00460 in
ASTM D1003
Transmission, Visible 87 %

@Thickness 0.178 mm
87 %

@Thickness 0.00700 in
TLT; ASTM D1003
88 %

@Thickness 0.102 mm
88 %

@Thickness 0.00400 in
TLT; ASTM D1003
88 %

@Thickness 0.127 mm
88 %

@Thickness 0.00500 in
TLT; ASTM D1003