BASF Elastollan® 1175A10W Wire & Cable Grade Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP
Manufacturer BASF
Trade Name Elastollan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Elastollan® 1175A10W Wire & Cable Grade Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation.
Physical Properties Metric English Comments
Density 1.14 g/cc

@Thickness 2.00 mm
 0.0412 lb/in³

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 75

@Thickness 2.00 mm
 75

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D2240
Tensile Strength, Ultimate 41.0 MPa

@Thickness 2.00 mm
 5950 psi

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D412
Tensile Strength, Yield 4.80 MPa

@Strain 100 %
 696 psi

@Strain 100 %
 ASTM D-412
11.0 MPa

@Strain 300 %
 1600 psi

@Strain 300 %
 0.76 mm (0.030 in) extruded sheet; ASTM D-412
Elongation at Break 685 %
685 %
on 0.030 in extruded sheet; ASTM D-412
Flexural Modulus 0.0250 GPa

@Thickness 2.00 mm
 3.63 ksi

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D790
Tear Strength 27.0 kN/m

@Thickness 0.760 mm
 154 pli

@Thickness 0.0299 in
 Split tear strength; extruded sheet; ASTM D-1938
Graves Tear Strength 57.0 kN/m

@Thickness 0.762 mm
 325 pli

@Thickness 0.0300 in
 extruded sheet; ASTM D624
Taber Abrasion, mg/1000 Cycles 20

@Thickness 2.00 mm
 20

@Thickness 0.0787 in
 H-18 wheel; ASTM D-1044; molded plaque, cured 20 hr at 100°C.
Compression Set 25 %
25 %
22 hr at 23°C per ASTM D-395; 2.0 mm (0.080 in) molded plaque, cured 20 hr at 100°C.
45 %

@Temperature 70.0 °C
 45 %

@Temperature 158 °F
 22 hr @ 70°C; ASTM D-395; 0.080 in molded plaque after curing 20 hrs at 100°C.
Tensile Set 32 %
32 %
at 200% elongation per ASTM D-412 is on 0.030 in extruded sheet.
Thermal Properties Metric English Comments
Vicat Softening Point 80.0 °C

@Thickness 2.00 mm
 176 °F

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C.; ASTM D1525
Glass Transition Temp, Tg -47.0 °C
-52.6 °F
Pellet sample
Flammability, UL94 V-2

@Thickness 1.59 mm
 V-2

@Thickness 0.0626 in
 Color: NC
V-2

@Thickness 3.14 mm
 V-2

@Thickness 0.124 in
 Color: NC
V-0

@Thickness 0.900 mm
 V-0

@Thickness 0.0354 in
 Color: NC