Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | Valox® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics Valox® 4012G PBT (Europe-Africa-Middle East).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
Filler Content | 10 % | 10 % | ASTM D229 |
Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
Viscosity | 110000 cP | 110000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | on Tensile Bar; SABIC Method |
0.0060 - 0.016 cm/cm @Thickness 3.20 mm |
0.0060 - 0.016 in/in @Thickness 0.126 in |
SABIC Method | |
Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | on Tensile Bar; SABIC Method |
Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 250 °C |
10 g/10 min @Load 2.65 lb, Temperature 482 °F |
ASTM D1238 |
90 g/10 min @Load 5.00 kg, Temperature 266 °C |
90 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
Hardness, H358/30 | 110 MPa | 16000 psi | ISO 2039-1 |
Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
5.0 % | 5.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
Tensile Modulus | 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 |
4.50 GPa | 653 ksi | 1 mm/min; ISO 527 | |
Flexural Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
120 MPa | 17400 psi | 2 mm/min; ISO 178 | |
Flexural Yield Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
125 MPa | 18100 psi | 2 mm/min; ISO 178 | |
Flexural Modulus | 3.80 GPa | 551 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
3.80 GPa | 551 ksi | 2 mm/min; ISO 178 | |
Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
0.500 J/cm @Temperature 0.000 °C |
0.937 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
0.500 J/cm @Temperature -30.0 °C |
0.937 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
Izod Impact, Unnotched | 3.80 J/cm | 7.12 ft-lb/in | ASTM D4812 |
3.80 J/cm @Temperature -30.0 °C |
7.12 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
5.00 kJ/m² @Temperature 0.000 °C |
2.38 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | ISO 179/2C |
4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
3.30 J/cm² @Temperature -30.0 °C |
15.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/2C |
0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 46.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
47.9 µm/m-°C @Temperature 23.0 - 150 °C |
26.6 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
>= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | |
Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
Dielectric Constant | 3.1 @Frequency 50.0 - 60.0 Hz |
3.1 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
ASTM D150 | |
3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 | |
Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
23.0 kV/mm @Thickness 1.60 mm |
584 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
23.0 kV/mm @Thickness 1.60 mm |
584 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
30.0 kV/mm @Thickness 0.800 mm |
762 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
30.0 kV/mm @Thickness 0.800 mm |
762 kV/in @Thickness 0.0315 in |
in oil; ASTM D149 | |
Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz |
0.0010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
ASTM D150 | |
Comparative Tracking Index | >= 150 V | >= 150 V | IEC 60112 |
325 V | 325 V | IEC 60112 |