SABIC Innovative Plastics LNP THERMOCOMP JF004ER PES (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP JF004ER PES (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* JF-1004 S-3 is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
Elongation at Break 2.4 %
2.4 %
5 mm/min; ISO 527
Tensile Modulus 7.10 GPa
1030 ksi
1 mm/min; ISO 527
Flexural Yield Strength 177 MPa
25700 psi
2 mm/min; ISO 178
Flexural Modulus 6.00 GPa
870 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 223 °C
433 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af