- Solvay Specialty Polymers AvaSpire® AV-848 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
Solvay Specialty Polymers AvaSpire® AV-848 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers AvaSpire® AV-848 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AvaSpire® AV-848 CF30 is a 30% carbon fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of PEEK. These include improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature.Features: Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High StrengthUses: Bearings; Bushings; Oil/Gas Applications; Seals; Wear StripInjection Molding Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | Carbon Fiber |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00 - 0.0020 cm/cm | 0.00 - 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 400 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 176 MPa | 25500 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 18.8 GPa | 2730 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 259 MPa | 37600 psi | ASTM D790 |
| Flexural Modulus | 16.5 GPa | 2390 ksi | ASTM D790 |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Shear Strength | 95.0 MPa | 13800 psi | ASTM D732 |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.0370 W/m-K | 0.257 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Melt Temperature | 382 - 404 °C | 720 - 759 °F | |
| Mold Temperature | 166 - 193 °C | 331 - 379 °F | |
| Drying Temperature | 149 °C @Time 14400 sec |
300 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
Users viewing this material also viewed the following:
- ACC QLE 1030 QSI Quantum Silicones 27 Durometer Addition Cure Elastomer for Coating (discontinued **)
- Ineos ABS Lustran® ABS 595CP Refrigeration and Extrusion Grade
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 4 lb
- Sinotek Materials MD-8 Graphite Emulsion
- Sax Polymers SAXAMID 126H Nylon 6, Injection Molding Grade
- ExxonMobil Exceed™ 1018EB Metallocene Polyethylene Resin (European Grade)
- Bales Mold Service Nicklon® Nickel-P.T.F.E. Mold Coating
- Bhansali Engineering Abstron HR-59 ABS Heat Resistant
- ExxonMobil Gargoyle Arctic 234 SHC 200 Series
- Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (7 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved