SABIC Innovative Plastics Ultem LTX300A PEI Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem LTX300A PEI Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D 792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.25 % @Temperature 23.0 °C |
1.25 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | on tensile bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.4 g/10 min @Load 6.60 kg, Temperature 295 °C |
2.4 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D 1238 |
| 15 g/10 min @Load 5.00 kg, Temperature 340 °C |
15 g/10 min @Load 11.0 lb, Temperature 644 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 127 MPa | 18400 psi | ISO 2039-1 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| 97.0 MPa | 14100 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 25 % | 25 % | 5 mm/min; ISO 527 |
| 30 % | 30 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| 3.31 GPa | 480 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
| 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 3.20 GPa | 464 ksi | 2 mm/min; ISO 178 |
| 3.24 GPa | 470 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.690 J/cm @Temperature 23.0 °C |
1.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 20.8 J/cm @Thickness 3.20 mm |
39.0 ft-lb/in @Thickness 0.126 in |
reverse notched; ASTM D 256 | |
| Izod Impact, Unnotched | 21.0 J/cm @Temperature 23.0 °C |
39.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Gardner Impact | 35.0 J @Temperature 23.0 °C |
25.8 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| Impact Test | 40.0 J @Temperature 23.0 °C |
29.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Taber Abrasion, mg/1000 Cycles | 15 @Load 1.00 kg |
15 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 187 °C @Thickness 3.20 mm |
369 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 189 °C @Thickness 6.40 mm |
372 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 200 °C | 392 °F | Rate B/50; ISO 306 |
| 200 °C | 392 °F | Rate B/120; ISO 306 | |
| 210 °C | 410 °F | Rate B/50; ASTM D 1525 | |
| 210 °C | 410 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 by SABIC-IP |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® DMX9254 PC (Asia Pacific)
- H.C. Starck Grade B Titanium Carbonitride
- Saint-Gobain CHR® C665 Copper Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- Formosa Plastics Formolene® L42009F Film (Butene Grade) LLDPE
- A. Schulman PP 828-31 Polypropylene Black Molding Grade Impact Polypropylene
- ChevronTexaco ISO 68 Ammonia Refrigeration Oil
- DuPont Performance Polymers Hytrel® HTR237BG BK320 Polyester Elastomer TPC-ET (Unverified Data**)
- Bulk Molding Compounds BMC A50-XHS High Strength Grade Molding Compound
Copyright © lookpolymers.com All Rights Reserved