SABIC Innovative Plastics ULTEM 2212EPR PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics ULTEM 2212EPR PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA lising.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0050 - 0.0070 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0050 - 0.0070 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15 g/10 min <br>@Load 6.60 kg,<br> Temperature 337 °C |
15 g/10 min <br>@Load 14.6 lb,<br> Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.79 GPa | 840 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 172 MPa | 24900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Yield Strength | 172 MPa | 24900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.10 GPa | 740 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 5.51 GPa | 799 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 12.0 J <br>@Temperature 23.0 °C |
8.85 ft-lb <br>@Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C <br>@Thickness 3.20 mm |
410 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 |
| 212 °C <br>@Thickness 6.40 mm |
414 °F <br>@Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C <br>@Thickness 3.20 mm |
401 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 |
| 207 °C <br>@Thickness 6.40 mm |
405 °F <br>@Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 210 °C | 410 °F | Rate B/50; ASTM D1525 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | V-0 <br>@Thickness 0.400 mm |
V-0 <br>@Thickness 0.0157 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Northstar Polymers MPG-023 Isocyanate Prepolymer
- ExxonMobil Iotek® 8610 Sodium Ionomer (discontinued **)
- Mitsubishi Xantar® F 22 R Polycarbonate
- Solvay Specialty Polymers Veradel® AG-330 Polyethersulfone (PESU), 30% Glass Fiber
- ExxonMobil Mobil Pegasus 15W-40 40
- Arkema Group Pebax® 4033 SP 01 Polyether Block Amide (PEBA)
- AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, Extra Deep Drawing Steel Plus (EDDS+), Standard Grade
- Gouda Vuurvast GOLITE MW Refractory Insulating Castable
- Styron Magnum™ 9020 ABS, High Gloss
Copyright © lookpolymers.com All Rights Reserved