Azoty Tarnow™ TARNOFORM 300 TF POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARNOFORM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARNOFORM 300 TF POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tribological modified grade low level addition of PTFE, which lower coefficient of friction and wear.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | ISO 527 |
| Elongation at Break | 47 % | 47 % | ISO 527 |
| Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.30 kJ/m² | 3.00 ft-lb/in² | 1A; ISO 180 |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | 1eA; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.48 J/g-°C | 0.354 BTU/lb-°F | |
| Melting Point | 167 °C | 333 °F | 10°C/min.; ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | ISO 75 |
| Vicat Softening Point | 150 °C | 302 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz |
3.4 @Frequency 1e+6 Hz |
IEC 60250 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243 |
| Dissipation Factor | 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 230 °C | 356 - 446 °F | Barrel temperature |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F |
Users viewing this material also viewed the following:
- Resin Technology Group Fusion 508 Industrial Grade Gel Fusion Cyanoacrylate
- DP7-3002 Polyurethane-based Biomedical Elastomer
- Huntsman HT 976 Aromatic Amine
- LG Chemical LUCON CP-4201F Conductive Thermoplastic, Flame Retardant
- Teknor Apex Flexalloy® 9100-55 Polyvinyl Chloride Elastomer
- Chase Plastics CP Pryme® A100 ABS Molding Resin
- ArcelorMittal AS60 Aluminized steel
- AIM 97In/3Ag Solder for Photonic Packaging
Copyright © lookpolymers.com All Rights Reserved