PolyOne Trilliant™ HC HC6600-0010 ESD Black Polyamide 66 (Nylon 66)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	PolyOne Corporation
Trade Name	Trilliant™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Trilliant™ HC HC6600-0010 ESD Black Polyamide 66 (Nylon 66).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.19 g/cc	1.19 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Elongation at Break	4.0 %	4.0 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	3.59 GPa	521 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	193 MPa	28000 psi	ASTM D790
Flexural Modulus	6.89 GPa	999 ksi	ASTM D790
Izod Impact, Notched	0.270 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.506 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Izod Impact, Unnotched (ISO)	17.9 kJ/m²	8.52 ft-lb/in²	ASTM D256

Electrical Properties	Metric	English	Comments
Volume Resistivity	10000 ohm-cm - 1e+05	10000 ohm-cm - 1e+05	ASTM D257
Surface Resistance	10000 ohm - 1e+05	10000 ohm - 1e+05	ASTM D257

Processing Properties	Metric	English	Comments
Melt Temperature	282 - 310 °C	540 - 590 °F

Descriptive Properties	Value	Comments
Features	Good Chemical Resistance
	High Stiffness
	Semi Crystalline
Filler / Reinforcement	Carbon Fiber Reinforcement, 10% Filler by Weight
Forms	Pellets
Generic Material	Nylon 66
Generic Name	Polyamide 66 (Nylon 66)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Computer Components
	Connectors
	Consumer Applications
	Electrical Housing
	Electrical/Electronic Applications
	Housings
	Medical Device Housings
	Medical/Healthcare Applications
	Sporting Goods