SABIC Innovative Plastics SABIC PPCOMPOUND G3220A PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND G3220A PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound G3220A is a general purpose, 20% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS is 209767996.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 50 mm/min, 1A; ISO 527 |
| 87.0 MPa | 12600 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 3.3 % | 3.3 % | Type I, 50 mm/min; ASTM D638 |
| 3.3 % | 3.3 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 4.90 GPa | 711 ksi | 1 mm/min; ISO 527 |
| 5.38 GPa | 780 ksi | 50 mm/min; ASTM D638 | |
| Flexural Modulus | 4.21 GPa | 611 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.50 GPa | 653 ksi | 2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D256 |
| Izod Impact, Unnotched | 6.01 J/cm | 11.3 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature -30.0 - 100 °C |
8.33 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 163 µm/m-°C @Temperature -30.0 - 100 °C |
90.6 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 151 °C @Thickness 3.20 mm |
304 °F @Thickness 0.126 in |
ASTM D648 | |
| Vicat Softening Point | 163 °C | 325 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® LE-0520-AM LDPE Extrusion Resin (discontinued **)
- SABIC Innovative Plastics ULTEM 2210EPR PEI (Asia Pacific)
- SABIC Innovative Plastics Valox® 855 PBT (Europe-Africa-Middle East)
- Samsung Cheil Industries Infino® XP-2165M PPS
- Teknor Apex Sinvicomp SFW 7500 Polyvinyl Chloride, Flexible
- ExxonMobil 15W-40 Exxon XD-3 Extra
- Zeon Chemicals Zealloy® 1422X14 Modifier for Thermoplastics
- Zircar Zirconia ZYC Zirconia Cylinders Insulation
- Cotronics Duralco™ 120 500°F Silver Filled Epoxy, Electrically Conductive
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 55% Cold Reduction
Copyright © lookpolymers.com All Rights Reserved