A. Schulman FORMION™ FI 341 Ionomer
| Category | Polymer , Thermoplastic , Ionomer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman FORMION™ FI 341 Ionomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| 0.012 - 0.016 cm/cm @Thickness 3.20 mm |
0.012 - 0.016 in/in @Thickness 0.126 in |
aged 48 hrs at 121°C; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | 15 sec delay; ISO 868 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
| Elongation at Break | 325 % | 325 % | ISO 527 |
| Flexural Modulus | 0.490 GPa | 71.1 ksi | Tangent; ISO 178 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 41.0 °C @Thickness 3.20 mm |
106 °F @Thickness 0.126 in |
ISO 75 |
Users viewing this material also viewed the following:
- MV Labs CA500 CaF2 Calcium fluoride
- PolyOne OnFlex™ S HF 90A-3S1988 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics Geloy XTWM206 ASA
- LATI LASTANE 50 G/40 40% Glass Fiber Reinforced Polyurethane (PUR) (discontinued **)
- Taiwan PU Corporation TPUI-ED71 General Grade, Injection Molding Polyester Base TPU
- Teknor Apex Monprene® MP 1580L1 Thermoplastic Elastomer
- Fainplast Compounds GK 89/2 Flexible PVC, Flame Retardant Sheathing Lead Free
- Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Cold Drawn 37.5% Plus Aging 649°C (1200°F)/4hr/FC to 579°C/4hr/AC
- Ashley Polymers Ashlene® 520-40G Nylon 66, 40% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved