SABIC Innovative Plastics SABIC PPCOMPOUND 7705 PP

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name SABIC PPCOMPOUND
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics SABIC PPCOMPOUND 7705 PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SABIC® PPcompound 7705 is a mineral filled, impact modified polypropylene TPO. This material combines impact resistance, scratch resistance, and heat stability with interior automotive UV stability. The IMDS is 16161010.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 22 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
ISO 868
Tensile Strength at Break 16.0 MPa
2320 psi
Type I, 50 mm/min; ASTM D638
17.0 MPa
2470 psi
50 mm/min, 1A; ISO 527
Tensile Strength, Yield 22.0 MPa
3190 psi
50 mm/min; ISO 527
23.0 MPa
3340 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 24 %
24 %
Type I, 50 mm/min; ASTM D638
32 %
32 %
50 mm/min; ISO 527
Elongation at Yield 4.4 %
4.4 %
50 mm/min; ISO 527
4.6 %
4.6 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.90 GPa
276 ksi
50 mm/min; ASTM D638
2.01 GPa
292 ksi
1 mm/min; ISO 527
Flexural Modulus 1.90 GPa
276 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.07 GPa
300 ksi
2 mm/min, 64mm span; ISO 178
Izod Impact, Notched 1.18 J/cm
2.21 ft-lb/in
63.5*12.7*3.2mm, Cut; ASTM D256
Izod Impact, Unnotched NB
NB
63.5*12.7*3.2mm, Cut; ASTM D4812
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*4mm, Cut; ISO 180/1A
3.00 kJ/m²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 80*10*4mm, Cut; ISO 180/1A
6.00 kJ/m²

@Temperature 0.000 °C
 2.86 ft-lb/in²

@Temperature 32.0 °F
 80*10*4mm, Cut; ISO 180/1A
Charpy Impact, Notched NB
NB
80*10*4mm, Cut; ISO 179/1eA
0.200 J/cm²

@Temperature -30.0 °C
 0.952 ft-lb/in²

@Temperature -22.0 °F
 80*10*4mm, Cut; ISO 179/1eA
Dart Drop, Total Energy 7.00 J

@Temperature -30.0 °C
 5.16 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak, -30°C @ 6.6 m/s; ASTM D3763
19.0 J

@Temperature 0.000 °C
 14.0 ft-lb

@Temperature 32.0 °F
 Instrumented Impact Energy @ peak, @ 6.6 m/s; ASTM D3763
22.0 J

@Temperature 23.0 °C
 16.2 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 59.0 µm/m-°C

@Temperature -30.0 - 100 °C
 32.8 µin/in-°F

@Temperature -22.0 - 212 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 148 µm/m-°C

@Temperature -30.0 - 100 °C
 82.2 µin/in-°F

@Temperature -22.0 - 212 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
80*10*4mm, Cut; ISO 75-1&2
112 °C

@Thickness 3.20 mm
 234 °F

@Thickness 0.126 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 59.0 °C
138 °F
80*10*4mm, Cut; ISO 75-1&2
57.0 °C

@Thickness 3.20 mm
 135 °F

@Thickness 0.126 in
 ASTM D648
Vicat Softening Point 130 °C
266 °F
10N, 50°C/hr; ISO 306