Polymer Property : Tensile Strength, Yield = 23.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	23.0 MPa	3340 psi	2.0 in/min; 0.125" thickness; ASTM D-638
Chevron Phillips MD6800 HIPS - High Impact Polystyrene  (discontinued **) Rubber modified high impact polystyrene.Applications:Displays and retail product shelvingDurable household applicationsThin to medium thickness parts that require a combination of high flow and good..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
Global PP-3375-RM Polypropylene Random Copolymer Description-medium stiffness, low melting temperatures, very good for seal Applications-fabricsInformation provided by Global Polymers Corporation.
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638-02
Ipiranga Petrochem GM 5240 PR HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638-02
Ipiranga Petrochem GM 9245 F HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
LyondellBasell Astryn BA45H Polypropylene Copolymer, Flame Retardant Key Features: medium melt flow, medium modulus, flame retardant polypropylene copolymer, UL 94 V-2 flames, good electrical properties and insulating characteristics, good aesthetics and colorability..
Tensile Strength, Yield	23.0 MPa	3340 psi	ISO 527-1, -2
LyondellBasell Hifaxâ„¢ RTA3263EUV/1 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ RTA3263EUV/1 fractional melt flow, 1,700 MPa flexural modulus, UV-stabilized, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent b..
Tensile Strength, Yield	23.0 MPa	3340 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics SABIC PPCOMPOUND 7705 PP SABICÂ® PPcompound 7705 is a mineral filled, impact modified polypropylene TPO. This material combines impact resistance, scratch resistance, and heat stability with interior automotive UV stabili..
Tensile Strength, Yield	23.0 MPa	3340 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON CD0001 PS LNP* STAT-KON* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Tensile Strength, Yield	23.0 MPa	3340 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON FX98500C PE (Asia Pacific) LNP* Stat-kon* FX98500C is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.
Tensile Strength, Yield	>= 23.0 MPa	>= 3340 psi
Sibur 23003-30T Superior Quality Polypropylene Copolymer For production of pipes for hot and cold water supply, sewerage, containers for shampoo, oil, milk, and packing products of low muddiness.
Tensile Strength, Yield	23.0 MPa	3340 psi
Silon Tabond 3012 Adhesive Resin TABOND 3012 is an LLDPE based adhesive resin.Characteristics: â€¢ Highest adhesion to aluminium, copper, brass and steel â€¢ Adhesion durability at elevated temperatures and pressure cycling p..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
Total PPC 5720WZ Polypropylene, Impact Copolymer TOTAL Petrochemicals Polypropylene 5720WZ is a nucleated impact copolymer with a Melt Flow index of 20 g/10 min.TOTAL Polypropylene 5720WZ is characterized by good stiffness, creep resistance, very ..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
A. Schulman POLYFORT™ PP 1930UX Extra High Flow, UV Stabilized Copolymer Polypropylene DescriptionPolyfort® PP 1930UX is an extra high flow, heat resistant, UV stabilized copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	23.0 MPa	3340 psi	50mm/min; ISO 527-2
Borealis BorPURE™ MB6561 High Density Polyethylene for Injection Molding BorPure™ MB6561 is a bimodal, high-density polyethylene intended for injection and compression molding. This grade combines excellent organoleptic properties, environmental stress crack resistance ..
Tensile Strength, Yield	23.0 MPa	3340 psi	ISO 527-2
Total PPC 11750 Polypropylene, Heterophasic Copolymer, Injection Molding Polypropylene PPC 11750 is a nucleated and controlled-rheology heterophasic copolymer with very high Melt Flow index of 50 g/10 min.Polypropylene PPC 11750 is characterized by good impact resistance..
Tensile Strength, Yield	23.0 MPa	3340 psi
Goodfellow Polyhydroxybutyrate/Polyhydroxyvalerate (PHB 88/PHV 12) See also PHB. PHB/PHV copolymers are used in preference to PHB homopolymer for general purposes (e.g. molding containers) in order to obtain a better balance of stiffness and toughness. PHV contents..
Tensile Strength, Yield	23.0 MPa	3340 psi	2 in/min, Type IV bar; ASTM D638
Chevron Phillips Marlex® 9005 HDPE Injection Molding Resin Resin Type: Hexene CopolymerCharacteristics: Moderate flowExcellent impact strengthExcellent ESCRGood warpage resistanceApplications: Industrial partsSeatsFood and household containersAgricultural p..
Tensile Strength, Yield	23.0 MPa	3340 psi	ISO 527-2/50
ExxonMobil PP7054L1 Polypropylene Impact Copolymer Product Description: A nucleated impact copolymer resin with medium flow. It is suitable for molding applications like consumer products, closures, containers, toys and rigid packaging applications..
Tensile Strength, Yield	23.0 MPa	3340 psi	ISO 527-2/50
ExxonMobil PP7085E1 Polypropylene Impact Copolymer Product Description: A nucleated impact copolymer resin with high flow, excellent stiffness/toughness balance and antistatic properties for good molding behavior. It is suitable for molding applica..
Tensile Strength, Yield	23.0 MPa	3340 psi	chs 2.0 in/min; ASTM D638
Diamond Polymers NPP25-1202 TF20 20% Talc Filled Copolymer Polypropylene, Impact Modified, High Heat, High Stiffness with UV and Paintable Versions Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
Braskem GM5340PR High Density Polyethylene Triple-layer coating for metallic pipes; Umbilical pipes for offshore oil field platforms; Jacketing for wires and for optic fiber metallic cables; Self-propelled irrigation pipes; Localized irrigat..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM-D638
Braskem GM7040G HDPE High Density Extrusion Polyethylene GM7040G is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for a gas pressurized line. It is produced with bimodal technology and has high molar mass..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0436T40L1 Talc Reinforced
Tensile Strength, Yield	23.0 MPa	3340 psi	Yield, 50/50 mm/min; ISO 527-1
Addcomp PRIEX® 12031 Maleic Anhydride Grafted HDPE Fields of application: Functionalised polyethylene to be used as compatibiliser for polymer blends or coupling agent for wood flour, natural fibres, or mineral filled polyolefins. Also suitable to r..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
Braskem Green PE SGM7746C Blow Molding and Monofilament High Density Polyethylene Lower greenhouse gas emissions100% made from renewable raw materialsPerformance and Competitiveness: Green Polyethylene has the same characteristics as petrochemical polyethyleneApplications: Mono..
Tensile Strength, Yield	23.0 MPa	3340 psi	Typical; ISO 527-1/2
Axion Polymers Axpoly® PS13 1011 High Impact Polystyrene PS13 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS13 range of resin co..
Tensile Strength, Yield	23.0 MPa	3340 psi	50 mm/min; ASTM D638
Carmel Olefins CAPILENE® SR 50 Polypropylene Impact Copolymer Description: CAPILENE® SR 50 is a medium melt flow rate impact copolymer for injection molding applications. This grade offers good balance of stiffness, impact strength and processability.Applic..
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
Tipco Tipcolene® FPC 30 PPC - 30% Calcium Carbonate Reinforced Polypropylene Copolymer 30% Calcium Carbonate Filled PP CopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Tensile Strength, Yield	23.0 MPa	3340 psi	5mm/min; ASTM D638
Mitsui TPX® RT18 XB Methylpentene Copolymer TPX® is a 4-methylpentene-1 based polyolefin with a unique combination of transparency, heat and chemical resistant qualities. TPX is used in a wide variety of applications, including: medical equi..
Tensile Strength, Yield	23.0 MPa	3340 psi	ISO 572-2
Total Lacqrene® 814(EU) High Impact Polystyrene  (discontinued **) LACQRENE® 814 is a PBDE free high impact, flame retardant polystyrene with excellent UV stability, rated UL 94 V0 @ 2mm and UL 94 5 VA @ 3mm.ApplicationCovers for electrical equipment, External cov..