Polymer Property : Tensile Strength at Break = 17.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527-1, -2
LyondellBasell Hifaxâ„¢ HSBMR246 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ HSBMR246 medium high melt flow, 1,500 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an outstanding balance of physical pro..
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527-1, -2
LyondellBasell Hostacomâ„¢ BR712GC Polypropylene Copolymer Description: Hostacomâ„¢ BR712GC conventional melt flow, 1,300 MPa flexural modulus, UV-stabilized, mineral-filled polypropylene copolymer has an excellent balance of stiffness, impact and weathe..
Tensile Strength at Break	17.0 MPa	2470 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCD771 PPE-TPE (Asia Pacific) Flexible, high tensile elongation, halogen-free extrusion grade intended for evaluation in applications such as cable jacket. Flame retardant performance capable of meeting UL VW-1 requirement. 80C ..
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP TH0815A LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP TH0815A PUR (Asia Pacific) LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527-2/50
ExxonMobil Exxtral™ CNU 013 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with good UV resistance designed for automotive exterior applications. Availability: Africa & Middle East, Asia Pacific, Europe, South..
Tensile Strength at Break	>= 17.0 MPa	>= 2470 psi	ISO R 527
Fainplast Compounds AP 88 Flexible PVC, Flame Retardant Insulation General purposes
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds GS 7325 Flexible PVC, Injection Molding for Technical Items Plugs
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds GS 90/T Flexible PVC, Injection Molding for Footwear Technical items for footwear
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PMP 81 Flexible PVC, Extrusion Modified with PU Under sheathing PVC/PU
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds MPH 78/H Medical Flexible PVC, Extrusion Technical tubes no DOP
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PH 70/AS Flexible PVC, Transparent Extrusion Food belt carriers
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PH 70/AT Flexible PVC, Transparent Extrusion Transparent sheath, UL 94 Class V1
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PK 91 Flexible PVC, Lead Free Fencing
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PM 9012 Flexible PVC, Extrusion Furniture border
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Arkema Group LOTRYL® 7 BA 01 Copolymer Ethylene - Butyl Acrylate LOTRYL® 7 BA 01 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. LOTRYL® 7 BA 01 is used for film coextrusion and lamination where sealab..
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0436W40L Wollastonite Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0437M30CL Mica Reinforced Coupled
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0334C10L Calcium Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0336C10L1 Calcium Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0336C20L Calcium Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0339C10L Calcium Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Addiplast Addilene PMD 50215 Polypropylene Copolymer High impact strength, high elongation at breakInformation provided by Addiplast.
Tensile Strength at Break	>= 17.0 MPa	>= 2470 psi	250mm/min; ISO 527
Borealis Supercure™ LS4201S Polyethylene Insulation Compound, Crosslinkable Supercure™ LS4201S is a crosslinkable natural polyethylene compound, specially designed for insulation applications. Applications: Supercure™ LS4201S is intended for insulation of XLPE High Volta..
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds MGS 86 Medical Flexible PVC, Injection Molding Connectors and special components
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds MPH 75/D Medical Flexible PVC, Extrusion Technical tubes no DOP
Tensile Strength at Break	17.0 MPa	2470 psi	UL 1581
SABIC Innovative Plastics NORYL WCD835 PPE-TPE (Asia Pacific) Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end..
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PM 92 Flexible PVC, Extrusion Semirigid profiles
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527
SABIC Innovative Plastics LNP Stat-kon MD000IU PP (Asia Pacific) LNP* Stat-kon* MD000IU is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact, UV Stabilized.This data wa..