- SABIC Innovative Plastics Noryl N190HX PPE+PS
SABIC Innovative Plastics Noryl N190HX PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl N190HX PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High gloss. 182F (83C) HDT. UL94 V-0/5VA rated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D 792 |
| Water Absorption | 0.066 % @Time 86400 sec |
0.066 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D 785 |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 14 % | 14 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 3.8 % | 3.8 % | Type I, 50 mm/min; ASTM D 638 |
| Tensile Modulus | 2.46 GPa | 357 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 2.27 GPa | 329 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature -30.0 °C |
1.50 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 1.92 J/cm @Temperature 23.0 °C |
3.60 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 18.69 J/cm @Temperature 23.0 °C |
35.01 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Impact Test | 11.0 J @Temperature -30.0 °C |
8.11 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Taber Abrasion, mg/1000 Cycles | 82 @Load 1.00 kg |
82 @Load 2.20 lb |
CS-17; ASTM D 1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 91.8 µm/m-°C @Temperature -40.0 - 95.0 °C |
51.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM C 177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| UL RTI, Electrical | 95.0 °C | 203 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 95.0 °C | 203 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.01 mm |
HB @Thickness 0.0398 in |
UL 94 |
| V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 | |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 35.7 % | 35.7 % | LOI; ASTM D 2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.00e+16 ohm-cm | 8.00e+16 ohm-cm | ASTM D 257 |
| Surface Resistance | >= 1.00e+11 ohm | >= 1.00e+11 ohm | ASTM D 257 |
| Dielectric Constant | 2.6 @Frequency 100000 Hz |
2.6 @Frequency 100000 Hz |
ASTM D 150 |
| Dielectric Strength | 28.1 kV/mm @Thickness 1.60 mm |
714 kV/in @Thickness 0.0630 in |
in oil; ASTM D 149 |
| Dissipation Factor | 0.0057 @Frequency 100000 Hz |
0.0057 @Frequency 100000 Hz |
ASTM D 150 |
| 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
ASTM D 150 | |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten, PLC code 7; ASTM D 495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | PLC code 1; UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC code 2; UL 746A |
| High Amp Arc Ignition, HAI | 30 - 60 arcs | 30 - 60 arcs | surface, PLC code 2; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | PLC code 4; UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Radiant Panel Listing | YES | UL Tested |
| UV-light, water exposure/immersion | F1 | UL 746C |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N 2845 GRN Acrylonitrile-Butadiene Rubber
- 3M Dyneon™ Fluorel™ FX-11818 Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **)
- SABIC Innovative Plastics Lexan® 143 PC (Europe-Africa-Middle East)
- Lotte Chemical Titan TITANLENE® LDF260GG Low density polyethylene
- SABIC Innovative Plastics LNP THERMOCOMP SF00A PA12 (Asia Pacific)
- Chesterton 421 Clear Protective Coating
- DuPont Teijin Films Mylar® LJP Polyester Film, 700 Gauge
- Carlson C 825 Nickel-Iron-Chromium Alloy
- Beijing Chemical Industry KAIFA® 301-G15RF PBT Resin
- DuPont Performance Polymers Neoprene FB Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved