SABIC Innovative Plastics Noryl GTX GTX8710 PPE+PA
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GTX GTX8710 PPE+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX8710 resin is a glass filled, high performance blend of PPE/PA that exhibits an exceptional balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D 792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0055 - 0.0065 cm/cm @Thickness 3.20 mm |
0.0055 - 0.0065 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 280 °C |
10 g/10 min @Load 11.0 lb, Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 11.7 g/10 min @Load 5.00 kg, Temperature 280 °C |
11.7 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D 638 |
| 100 MPa | 14500 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D 638 |
| 100 MPa | 14500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D 638 |
| 4.5 % | 4.5 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D 638 |
| 4.5 % | 4.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.00 GPa | 725 ksi | 5 mm/min; ASTM D 638 |
| 5.00 GPa | 725 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 165 MPa | 23900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.30 GPa | 624 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 4.30 GPa | 624 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.650 J/cm @Temperature -30.0 °C |
1.22 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.900 J/cm @Temperature 23.0 °C |
1.69 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 28.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 82.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 82.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 210 °C | 410 °F | Rate B/50; ASTM D 1525 |
| 210 °C | 410 °F | Rate B/50; ISO 306 | |
| 210 °C | 410 °F | Rate B/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | SABIC Method |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® XHT1141 PC (Asia Pacific)
- Hyosung Topilene C600 PP
- Flint Hills P6G4Z-097 Impact Copolymer Polypropylene
- SABIC Innovative Plastics ULTEM ATX200F PEI (Europe-Africa-Middle East)
- Shandong Dongyue Shenzhou New Material Co DS602 Perfluorinated Ethylene-Propylene Copolymer
- SABIC Innovative Plastics NORYL GFN3 PPE+HIPS (Europe-Africa-Middle East)
- Styron CALIBREâ„¢ 300-6 Polycarbonate Resin
- SCG Chemicals EL-Leneâ„¢ L2009F Linear Low Density Polyethylene Film
- Orion Engineered Carbons CORAX® HP 160 HP Carbon Black
- Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched
Copyright © lookpolymers.com All Rights Reserved