SABIC Innovative Plastics NORYL LTA6020 PPE+PS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL LTA6020 PPE+PS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Melt Flow 4.0 g/10 min

@Load 10.0 kg,
Temperature 250 °C
 4.0 g/10 min

@Load 22.0 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 8.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
20 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 20 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 57.0 MPa
8270 psi
50 mm/min; ISO 527
Tensile Strength, Yield 71.0 MPa
10300 psi
50 mm/min; ISO 527
72.0 MPa
10400 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 8.0 %
8.0 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.68 GPa
389 ksi
1 mm/min; ISO 527
Flexural Yield Strength 105 MPa
15200 psi
2.6 mm/min, 100 mm span; ASTM D790
105 MPa
15200 psi
2 mm/min; ISO 178
Flexural Modulus 2.58 GPa
374 ksi
2.6 mm/min, 100 mm span; ASTM D790
2.60 GPa
377 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.20 J/cm
4.12 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -40.0 °C
 3.81 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature -20.0 °C
 4.76 ft-lb/in²

@Temperature -4.00 °F
 80*10*4; ISO 180/1A
11.0 kJ/m²

@Temperature -10.0 °C
 5.23 ft-lb/in²

@Temperature 14.0 °F
 80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature 0.000 °C
 5.71 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
Charpy Impact Unnotched 1.80 J/cm²
8.57 ft-lb/in²
ISO 179/2C
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Hot Ball Pressure Test 125 °C
257 °F
IEC 60695-10-2
<= 135 °C
<= 275 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 123 °C
253 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
126 °C

@Thickness 6.40 mm
 259 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 144 °C
291 °F
Rate B/120; ISO 306
155 °C
311 °F
Rate A/120; ISO 306
UL RTI, Electrical 125 °C
257 °F
UL 746B
UL RTI, Mechanical with Impact 125 °C
257 °F
UL 746B
UL RTI, Mechanical without Impact 125 °C
257 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.00 mm
 V-1

@Thickness 0.0394 in
 UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
5VA

@Thickness 2.50 mm
 5VA

@Thickness 0.0984 in
 UL 94
Glow Wire Test 825 °C
1520 °F
IEC 60695-2-13
825 °C
1520 °F
IEC 60695-2-13
825 °C
1520 °F
IEC 60695-2-13
825 °C
1520 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A